Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Question

Want to see the full answer?

Answer 1

Question

Chapter 10.9, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Students have asked these similar questions

Two W14x38 tension members are connected with a splice connection using plates attached atthe top and the bottom flanges. The design axial load Pu is 320 kips. The bolts are made of A325X, and thebolt diameter is ½ inch. (Slip-Critical connection)( LRFD units)

A tension member made of L4x4x1/2 is connected to gusset plate with welds. Using E70electrode and ½ inch weld size, design the balanced weld lengths.( Use AISC manual, LRFD units)

An office building is planned with a lateral-force-resisting system designed for earthquake resistance in aseismic zone. The seismic capacity of the proposed system, expressed as a force factor, is assumed tofollow a lognormal distribution with a median of 6.5 and a standard deviation of 1.5. The ground motionfrom the largest expected earthquake at the site is estimated to correspond to an equivalent force factor of 5.5.(a) What is the estimated probability that the building will experience damage when subjected to the largest expected earthquake? (b) If the building survives (i.e., experiences no damage) during a previous moderate earthquake with aforce factor of 4.0, what is the updated probability of failure of the building under the largest expectedearthquake?(c) Suppose future occurrences of the largest expected earthquake follow a Poisson process with a mean return period of 500 years. Assuming that damage events from different earthquakes are statisticallyindependent,…

Answer 2

Question

Chapter 10.9, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 3

Question

Chapter 10.9, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 4

Question

Chapter 10.9, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 5

Chapter 10.9, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Answer 6

Chapter 10.9, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Answer 7

Chapter 10.9, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Answer 8

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Answer 9

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Answer 10

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Answer 11

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Answer 12

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Answer 13

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Answer 14

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Answer 15

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Answer 16

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Answer 17

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Answer 18

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Answer 19

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Answer 20

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Answer 21

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Answer 22

Expert Solution & Answer

Answer 23

Expert Solution & Answer

Answer 24

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 25

Ch. 10.9 - Prob. 1QP Ch. 10.9 - Prob. 2QP Ch. 10.9 - Prob. 3QP Ch. 10.9 - Prob. 4QP Ch. 10.9 - Prob. 5QP Ch. 10.9 - Prob. 6QP Ch. 10.9 - Prob. 7QP Ch. 10.9 - Prob. 8QP Ch. 10.9 - Prob. 9QP Ch. 10.9 - Prob. 10QP

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Want to see the full answer?

Chapter 10 Solutions

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.