You have been asked to draw up a specification for a ceramic cladding tile that is likely to experience tensile stressesof 89 MPa during its installation and service lifetime.If the ceramic has a specific surface energy of 0.35 J/m2 and its Youngs Modulus is 85 GPa what would be themaximum length of an internal flaw that would not result in fracture of the tile?(This question has only one correct answer)a. 2.53 µmb. 5.06 µmc. 4.78 μmd. 2.53 mme. 2.39 mmf. 4.78 mmg. 2.39 um

Critical stress formula in terms of Youngs Modulus, surface energy and crack length is used.

You have been asked to draw up a specification for a ceramic cladding tile that is likely to experience tensile stresses of 89 MPa during its installation and service lifetime. If the ceramic has a specific surface energy of 0.35 J/m² and its Youngs Modulus is 85 GPa what would be the maximum length of an internal flaw that would not result in fracture of the tile? (This question has only one correct answer) a. 2.53 μm O b. 5.06 µm Ο c.4.78 μm O d. 2.53 mm O e. 2.39 mm f. 4.78 mm g. 2.39 µm

You have been asked to draw up a specification for a ceramic cladding tile that is likely to experience tensile stresses of 89 MPa during its installation and service lifetime. If the ceramic has a specific surface energy of 0.35 J/m² and its Youngs Modulus is 85 GPa what would be the maximum length of an internal flaw that would not result in fracture of the tile? (This question has only one correct answer) a. 2.53 μm O b. 5.06 µm Ο c.4.78 μm O d. 2.53 mm O e. 2.39 mm f. 4.78 mm g. 2.39 µm

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Sintered silicon nitride parts are expected to experience tensile stresses 50% of the ultimate tensile strength of the material. What will be the maximum allowable size of internal flaws for these parts not to fail in service? Given the following properties of the material: Specific surface energy: 0.3 J/m2 its Youngs Modulus: 304 GPa Ultimate tensile Strength: 570 MPa Select one: a. 1.43 µm b. 0.71 µm c. 15 µm d. 85 µm e. 9.5 µm
A mechanical component is fabricated from a metallic alloy. From the experiment, it is obtained that the fracture of this material occured at a stress of 36 ksi when the maximum internal crack length is 0.10 in. The plain strain fracture toughness of this material is 30 ksi sqrt(in) for this same component and alloy, investigate whether fracture will occur at stress level of 55 ksi when the internal crack length is 0.06 in.
Estimate the theoretical fracture strength of a brittle material if it is known that fracture occurs by the propagation of an elliptically shaped surface cra of length 0.5 mm and having a tip radius of curvature of 0.005 mm, when a stress of 1040MPa is applied. Your answer must be in GPa. Write your answer to 1 decimal place. Answer: V 30 (0) 00 a W 4340 steel alloy. Determine the ductile to brittle transition
A test specimen data made of polyvinyl chloride with 10.16-mm-diameter were collected (l. = 50.80 mm) and shown in Table 1. After fracture, the total length was extended to 53.08 mm and the diameter was 9.98 mm. Load (kN) Al (mm) 0 0.00 1.35 0.19 2.65 0.40 4.00 0.60 5.35 0.81 6.65 1.17 7.35 1.78 (maximum load) 7.10 2.39 6.30 3.05 (fracture) Table 1: The results of the tensile test for polyvinyl chloride. Plot the engineering stress-strain curve (list the stress and strain value in a Table) and evaluate: (i) (ii) the 0.2% offset yield strength; the modulus of elasticity; (iii) the percentage of reduction in area; (iv) the engineering stress at fracture; (v) the modulus of resilience.
QUESTION 1 Select from the following statements, those which describe the process and conditions required for brittle fracture. (Note: Partial credit is not available for this question. Credit will only be awarded if all correct answers, and no incorrect answers, are selected). A. Occurs along defined crystallographic planes, thus leaving smooth fracture surfaces B. Occurs due to repeated loading and unloading below the yield strength of the material OC. Occurs in materials where the bonding strength is high relative to the yield strength D. The stress concentration at the crack tip exceeds the inter-atomic bonding energy ☐ E. Involves the nucleation, growth and coalescence of voids, thus resulting in rough fracture surfaces OF. Is a slow process whereby there is warning prior to failure
Please solve
Interpret the following properties of brittle fracture and ductile fracture in terms of: Fracture surface Energy absorption
Computational analysis has determined that a particular design of glass ceramic component has a maximum allowable tensile stress of 16 MPa Your development team has suggested that a specific grade of Wollastonite with a Youngs Modulus of 89 GPa and a specific surface energy of 0.059 J/m² may be suitable. What would be the maximum allowable size of any internal pores or defects in the glass ceramic component? (This question has only one correct answer) O a. 13.79 mm O b. 26.12 mm O c. 13.06 mm O d. 27.58 μm e. 13.79 μm O f. 26.12 μm O g. 13.06 μm
Calculate the compressive strength for a ceramic containing crack of size100 µm. Let μ be the coefficient of friction between the flaw walls and ℓ be the length of the cracks generated at the ends of an existing flaw.Assume that the onset of failure corresponds to a value of ℓ= 2a and that μ = 1, and that KIc = 4 MN m1/2
In designing a ceramic part for a jet engine, to ensure that the part does not fail, we plan to ensure that the maximum applied stress is only one-third of the yield strength. The yield strength of this CMC part for a jet engine is 520 MPa, and its plane strain fracture toughness is 5.5 MPa√?. We utilize a nondestructive test to find any internal faults that are longer than 1.27 mm. Does our non-destructive test have the requisite sensitivity if Y = 1.4? Explain.
Need help on this Q
1. For the stress-strain curve shown below, please estimate the properties indicated. (a) Fracture Strain Please do your work on a separate sheet of paper, and put your answers in the boxes on the right. Be sure to include the proper symbol and units. Stress Strain 70 60 50 Stress (ksi) 240 30 20 10 70 0 0.000 60 50 Stress (ksi) 40 20 10 KULL 0 0.000 0.010 0.050 0.100 Strain (in/in) Stress Strain 0.020 0.030 Strain (in/in) 0.040 0.150 0.050 (b) Ultimate Tensile Stress (c) Fracture Stress (d) Proportional Limit (e) Elastic Modulus (1) Yield Stress (g) Tensile Toughness (Modulus of Toughness) (h) Modulus of Resilience