Answered: Which of the following phase will be…

Engineering

Mechanical Engineering

Which of the following phase will be resulted when the transformation temperature of steel is more than 750 °C?

Precision Machining Technology (MindTap Course List)

2nd Edition

ISBN:9781285444543

Author:Peter J. Hoffman, Eric S. Hopewell, Brian Janes

Publisher:Peter J. Hoffman, Eric S. Hopewell, Brian Janes

Chapter2: Measurement, Materials, And Safety

Section2.7: Heat Treatment Of Metals

Problem 4RQ: What type of hardening operation that leaves the inner core in a softer condition is sometimes...

See similar textbooks

Similar questions

What type of hardening operation that leaves the inner core in a softer condition is sometimes performed on medium-carbon steels?
Part C. Which type of phase transformation is important in heat treatment of steels? (circle one)Peritectic Eutectic Eutectoid Incongruent meltingAt what temperature and overall composition wt% C, does it occur?Write the reaction equation for this transformation, and briefly describe the nature of each of the three important phases that are involved.
Austentitic stainless steel's are not hardenable by cold working however Austentic stainless steel's can be strengthened by heat treatment true or false?
Using the time-temperature-transformation diagram, what steel phases would you generate by cooling from 900ºC A. quenching in cold water to 520ºC in 0.5 second, holding the sample temperature constant for 1000 seconds at 520ºC, and then quenching to room temperature B. cooling down to room temperature over a period of 2 weeks?
Below is a continuous cooling transformation curve for steel (upper) and for a silicate melt (lower). Describe the similarities and differences as follows. a. What is the critical cooling rate in each case? b. What phase(s) form in each case when the critical cooling rate is exceeded? c. What phase(s) form in each case if the cooling rate is very slow? 800 1400 Ae lemperature Austenite *peorlite begins 10FI 700 1200 Austenitepearlite complete 1600 1000 5009 800 Tronsformation stops 400 600 300 400 Austenite -mortenstic structure 200 -Isathermal dogram Continuous transformaton diogrom Constant rate coding curves - 100 200 Findl structure Mortensite Morlensite i peorlile Peorite (softer, coorser- 0.1 10? 10 Tronsformation time, seconds Continuous Cooling-Transformation (C-T)Diagram (Derived from the isothermal-transformation diagram for a plain-carbon eutectoid steel) 1200 Glass Crystallization begins 1100 1000 Critical cooling rate Glass-ceramic 900 Crystallization ends 800 700 102 10…
Using the TTT diagram for eutectoid steel, draw the specified cooling path on the diagram. Indicate what phases you expect in the final product with percentage of each phase. Assume the material has been fully austenitized before cooling. a. Water cool to room temperature b. Hot quench in molten salt to 690°C and then cooled isothermally for 2 hours: c. Hot quench to 610°C hold 3 minutes and water quench
A-What is the purpose of the following heat treatments?(mention two points only for each heat treatment). 1-tempering.2-Annealing. 3-surface hardening.
Why does the hardness decrease at 600 ° C after rising when the tempering process
What is the microstructure that will be formed after heat treatment of steel containing 1.4 carbon ratio with normalization and air cooling? support with phase diagram and TTT diagrams.
1. Annealing is carried out to relieve stresses II. Annealing is carried out to increase softness III. Annealing is carried out to produce a specific microstructure IV. Annealing is always utilized in low carbon steels Which statement(s) is/are true given above about annealing processes?
1-Compact Graphite cast iron was obtained from fast cooling rates.? T F 2-Strength and ductility of nodular iron approximately the same under tension and compressive loads.? T F 3-The grey should be heated to 700 oC for 30 hours to obtain malleable iron? T F 4-The carbon in CGI alloys is neither flakes nor cementite? T F 5-Exhaust manifold manufactured from white cast iron.? T F 6-The reduced section length of the tensile specimen should be at least four times the diameter.? T F 7-Tangent modulus is taken as the slope of the stress–strain curve at yield stress? T…
Indicate which microstructures will appear after each induction hardening process step: Options: ( martensite, tempered martensite, bainite, pearlite, austenite) a. tempering. b. Quenching c. Induction heating