Phase diagram is of a Copper-Iridium alloyAnswer choices:a) Monotecticb) Eutecticc) Eutectoidd) Peritectice) None of the above Which invariant reaction can be recognized in the phase diagram shown here?25002300210-19001700150013001138110010100Cuat. %IrTemperature, "C

the peritectic reaction can be easily recognized in the phase diagram.

Answered: Which invariant reaction can be…

Engineering

Mechanical Engineering

Which invariant reaction can be recognized in 2300 210 1900 1700 1500 1300 Temperature, "C (A)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Question One (Compulsory) Composition (atk Sn) 100 20 40 60 80 327C B00 300 Liquid 500 232C 400 200 183C 07.8 18.3 61.9 300 100- H200 100 BO 100 20 40 60 Pb) Compesition (wt% Sn) Figure 1: Lead -tin phase diagram Figure I above shows a lead-tin (alloy) phase diagram. Consider an alloy composition of 55 wt% Sn - 45 wt% Pb. Answer the following questions: (i) Name the phases present and their compositions in the alloy at 150°C. (ii) Describe the structural and composition changes in the alloy when it is cooled from 190°C to 20°C. (iii) What are the compositions of phases at the eutectic point and why is this point important for the alloy? (iv) Given that the average density of a phase is determined as Pa = 100 ,calculate the PA PB volume fractions of the phases at the given compositions and at 150°C. Take the densities of lead and tin as 11.34 g/cm' and 7.36 g/cm' while the mass fraction of a is 0.21. (v) Name and describe four industrial applications of lead-tin alloys. ta aroundu (3.)…
Temperature (°C) 700 600 0 500 400 300 0 (AI) a 5 a+L 10 Composition (at% Cu) 10 20 a +0 L 30 Composition (wt% Cu) 20 0+ L 0 (CuAl₂) 40 30 50 1200 1000 800 600 Temperature (°F) a) For the alloy represented by the phase diagram above, what is the wt% content of eutectic if an alloy of 2.5 wt% Cu is cooled very slowly from the molten state to 300°C? b) What phases are present in 2.5 wt% Cu material if it is quenched from 550°C?
Question 4 A segment of the Fe/C alloy phase diagram is shown below: Composition (at% C) 15 Temperature (°C) 0 1600 1400 1200 1000 800 600 400 1538°C 0 (Fe) 8 Y 912°C -1493 C 1394-C Y. Austenite 0.76 0.022 a, Ferrite 1 y+L 2 2.14 10 1147 C at Fe₂C L 4.30 Y+Fe3C 4 3 Composition (wt% C) 727°C 20 Cementite (Fe-C) 5 6 25 2500 2000 1500 1000 6.70 Temperature (°F) a) What are the equilibrium phases, compositions and relative fractions of the Fe-C alloy at an average composition Ccarbon of 2% and a temperature of 730 °C? b) What are the equilibrium phases, compositions and relative fractions of the Fe-C alloy at an average composition Ccarbon of 2% and a temperature of 725 °C? 7 c) Sketch the microstructure of the alloy obtained by quick cooling of the alloy from the conditions in part a) to the conditions in part b). Be sure to identify the phases in your sketch.
Kindly answer all Tempering of a plain carbon steel is defined as a) rapid quenching of the annealed metal b) cold working of the annealed metal c) reheating the austenitized and quenched metal to an intermediate temperature d) reheating the annealed metal to an intermediate temperature Initial focusing of the reflective light microscope is done with a) a low magnification lens and the field diaphragm open b) a low magnification lens and the field diaphragm closed c) a high magnification lens and the field diaphragm open d) a high magnification lens and the field diaphragm closed Which of the following hot rolled steels would have the most ferrite in its microstructure? a) C1020 b) C1040 c) C1060 d) C1080 Which of the following hot rolled steels would have the most pearlite in its microstructure? a) C1020 b) C1040 c) C1060 d) C1080
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13 wt. % C steel with no alloying elements. part A) quenched in cold water directly to room temperature in 0.1 second part B) quenched in cold water directly to room temperature in 0.1 seconds, then heated to 425 C and held there for 1000 seconds, and finally quenched to room temperature part C) quenched in cold water to 670 C in 0.1 seconds, then held at 670 C for 1000 seconds, then quenched to room temperature part D) quenched in cold water to 650 C in 0.1 seconds, then held at 650 C for 5 seconds, then quenched to 400 C, held at 400 C for 60 seconds, and finally quenched to room temperature
5. [Phase Diagram] (1) Here is Cu-Ag phase diagram and two cases (composition and temperature) are given below. At each case, (i) cite the phase(s) present(s), (ii) estimate the phase composition(s), (iii) weight fraction of the phase(s) and (iv) sketch its microstructure for the following alloy. () a. 71.9 wt% Ag-28.1 wt% Cu at just above 779 °C b. 71.9 wt% Ag-28.1 wt% Cu at just below 779 °℃ Temperature (°C) 1200 A 1000 800 600 400 0 200 0 α C (Cu) B 8.0 (Ca E) -Solidus Solvus 20 20 a + L Composition (at% Ag) -Liquidus 779°C (TE) 40 40 a + B Liquid 60 Composition (wt% Ag) 60 E 71.9 (CE) 80 80 B+L 91.2 (CBE) G 100 B H 2200 2000 1800 F 1600 1400 1200 1000 800 600 400 100 (Ag) Temperature (°F)
Option: -SC plane 110 -SC plane 100 -FCC plane 111 -SC plane 111 -FCC plane 110 -BCC plane 100 -BCC plane 111 -FCC plane 100 -None of the provided choices -BCC plane 110 could you please tell me how to get the answer
Composition lat% N 40 60 100 1600 2800 1500 1453 C 2600 Liquid 1400 Solidus line Liquidua line 2400 1300 1200 2200 1100 1085 C 2000 1000 20 40 100 Composition (wt N (NO What is the amount for each phase in 1kg of a 50% Ni-50% Cu alloy at temperatures of 1400, 1300, or 1200 degrees C for point A and point B? Temperature ('C) Temperature ("F)
T or F -In the hypereutectoid steel alloy, the primary phase is Cementite ( iron carbide ) -In the Pb-Sn hypoeutectic alloy, the primary phase is the α-phase -The eutectic composition of the solder alloy is 98%wt Sn -In the steel alloys, the weight percent of the alloying elements affects the eutectoid temperature and Ceutectoid wt%C -Austenite phase has a BCC crystal structure The microstructure is characterized by: a.The number of phases present b.The present phases’ proportions. c.How these phases are arranged or distributed d.all of the answers
1) Draw the iron-Fe;C phase diagram. Consider 0.25 and 1.1 wt% C steel alloy. It is cooled slowly from atemperature within austenite phase to room temperature. Show a) microstructure at 1000 °C b) microstructure at 730°C c) microstructure at 715°C and d) microstructure at room temperature e) What do you say about mechanical properties of these alloys, depending on their microstructure at room temperature?
a) The figure below shows three equilibrium structures that occur in an iron-carbon alloy, rank these from hardest to softest. b) The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite. Relative mass to proeutectoid ferrite is 0.2 and pearlite is 0.80. How much carbon does this alloy contain?