When kaolinite clay [Al2(Si₂O5)(OH)4] is heated to a sufficiently high temperature, chemical water is driven off. (a) Under these circumstances, what is the composition of the remaining product (in weight percent Al2O3)? (b) What is the liquidus temperature of this material? (c) What is the solidus temperature of this material? You may want to use the SiO2-Al2O3 phase diagram (Animated Figure 12.25) to solve this problem. The following atomic weight data may be helpful AAI = 26.98 g/mol Asi = 28.09 g/mol Ao = 16.00 g/mol (a) (b) i (c) i wt% °C °C

When kaolinite clay [Al2(Si₂O5)(OH)4] is heated to a sufficiently high temperature, chemical water is driven off. (a) Under these circumstances, what is the composition of the remaining product (in weight percent Al2O3)? (b) What is the liquidus temperature of this material? (c) What is the solidus temperature of this material? You may want to use the SiO2-Al2O3 phase diagram (Animated Figure 12.25) to solve this problem. The following atomic weight data may be helpful AAI = 26.98 g/mol Asi = 28.09 g/mol Ao = 16.00 g/mol (a) (b) i (c) i wt% °C °C

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A NIO-20 mol % Mgo ceramic is allowed to solidify. (See the figure below.) Temperature (°C) 2800 2600 2400- 2200 2000 L (Ni, Mg)0 40 60 80 MgO Mole percent MgO NIO 20 (a) Determine the composition (in mol% MgO) of the first solid to form. 80 x (b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions. 35 X%
Consider de-oxidation by the addition of ferromanganese (60 percent Mn) to molten steel at 1600°C.The initial oxygen content is 0.04 wt%. It has to be brought down to 0.02 wt%. Calculate the quantity of ferromanganese required per tonne of steel. The manganese content of steel before de- oxidation is 0.1 wt%. (MnO) + [Fe] = [Mn] + (FeO) Given: K Mn at 1873 K = 0.4 K Fe-Mn at 1873 K = 0.156 Assumptions: Fe and Mn form ideal solutions
During freezing of a Cu-Zn alloy, we find that the composition is non-uniform. By heating the alloy to 600°C for 3 hours, diffusion of zinc helps to make the composition more uniform. What temperature would be required if we wished to perform this homogenization treatment in 30 minutes?
In a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the total and partial phases? Given:Eutectoid temperature=723°C; Eutectoid concentration=0.76% C; Limit concentration of ferrite=0.022%; Limiting concentration of cementite: 6.7%.
In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.
Iron (Fe) undergoes an allotropic transformation at 912°C: upon heating from a BCC (α phase) to an FCC (γ phase). Accompanying this transformation is a change in the atomic radius of Fe—from RBCC = 0.12584 nm to RFCC = 0.12894 nm—and, in addition, a change in density (and volume). Compute the percentage volume change associated with this reaction. Indicate a decreasing volume by a negative number.
Problem 2 Determine the carburizing time necessary to achieve a carbon concentration of 0.45 wt% at a position 2 mm into an iron-carbon alloy that initially contains 0.20 wt% C. The surface concentration is to be maintained at 1.30 wt% C, and the treatment is to be conducted at 1000 °C. Use the diffusion data for y-Fe in Table 5.2.
Determine the carburizing time necessary to achieve a carbon concentration of 0.50 wt% at a position 1.2 mm into an iron-carbon alloy that initially contains 0.18 wt% C. The surface concentration is to be maintained at 1.1 wt% C, and the treatment is to be conducted at 1200°C. Assume that Do 6.5 x 10-5 m2/s and Qd = 168 kJ/mol. The following table may be useful. %3D Table 5.1 Tabulation of Error Function Values erf(z) erf(z) erf(z) 0.55 0.5633 1.3 0.9340 0.0282 0.0564 0.025 0.60 0.6039 1.4 0.9523 0.05 0.10 0.65 0.70 0.75 0.6420 1.5 0.9661 0.1125 0.6778 1.6 0.9763 0.15 0.1680 0.7112 1.7 0.9838 0.20 0.2227 0.80 0.7421 1.8 0.9891 0.85 0.90 0.25 0.2763 0.7707 1.9 0.9928 0.9953 0.9981 0.30 0.3286 0.7970 2.0 0.35 0.3794 0.95 0.8209 2.2 0.8427 0.8802 0.40 0.4284 1.0 2.4 0.9993 0.45 0.4755 1.1 2.6 0.9998 0.50 0.5205 1.2 0.9103 2.8 0.9999
A mixture of 1.0 mol of hexane and 1.0 mol of nitrobenzene was prepared at 290 K. Calculate the amount of hexane present in each phase at 290 K by using the phase diagram given below. (nala = nglp) T/K P= 1 290 P= 2 273 0.17 ㅇ 0.2 0:65 0.8 0.6 0.4 1 x(C;H14)
A student performing this lab experiment receives his unknown solution that may contain ( Ba, Ca, and Mg). And begins to conduct tests to identify 2+ 2+ 2+ the cations present in the unknown solution. Based on the following observation 1) When the unknown solution was treated with K,Cro4, no precipitate was formed. 2) The resulting solution from step 1 was basified with 6M NH, before the addition of aqueous K,C,0, which forms a white precipitate. 3) To the resulting solution from step 2, was treated with ammonia and of Na,HPO,· A white precipitate 4 was formed after heating the solution for 10 minutes at 60°C. Which cations were present in the student's unknown solution? Select one or more: 2+ Ва 2+ Mg 2+ Са
Determine the carburizing time necessary to achieve a carbon concentration of 0.50 wt% at a position 3.1 mm into an iron-carbon alloy that initially contains 0.12 wt% C. The surface concentration is to be maintained at 1.2 wt% C, and the treatment is to be conducted at 1080°C. Assume that Do = 5.8 x 10-5 m²/s and Qd = 156 kJ/mol. The table Tabulation Error Function Values may be useful.
•You are case-hardening a tool made of BCC (α) iron in the presence of a carbonaceous material. A heat treatment at 600 oC for 100 minutes results in a carbon concentration of 0.75 wt% at a position 0.5mm below the surface. How long would it take to obtain the same concentration at the same position if the heat treatment were conducted at 900 oC? x12/D1t1= x22/D2t2 Arrhenius equation: D=D0e^(〖-Qd〗∕RT) Qd = Activation energy of diffusion D0 = Pre-exponential diffusion factor R = gas constant = 8.314 J/(mol*K) Use the Arrhenius equation to calculate D1 and D2. Calculate the time to satisfy the problem statement.