What is the microstructure seen in the sem images of ASTM A128 (high manganease casting) x10020.0kV LED100μm Guest2023/04/24WD 10.0mm 13:54:05SEM x1,00020.0kV LED10μmSEMGuest2023/04/24WD 10.0mm 13:44:05

The image shown is of grain boundaries separated micro structure. Tempered structure.

Answered: What is the microstructure seen in the…

Engineering

Mechanical Engineering

What is the microstructure seen in the sem images of ASTM A128 (high manganease casting)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: (b) What are the factors that affecting the freezing rate during solidification of the molten metal…

A: Chvorinov's rule: According to this law, the freezing rate (solidification time) is a function…

Q: How much time (in seconds) is required for austenite to transform to 50% bainite at 300°C? 800 727…

A: From the given graph, at 300oC temperature horizontal line, check the time corresponding to 50%…

Q: A rod-shaped single crystal of pure iron is to be tested in tension. The tensile axis is: [uvw] =…

A: Write the given data. Tensile axis: u v w=1 2¯ 0Slip plane: h1 k1 l1=1 1 0Slip direction: <u1 v1…

Q: Draw a diagram of the gray and nodular gray cast iron's substructure. 2. Comment on the gray…

A: Given data:- gray and nodular gray cast iron gray wrought iron's To be explained:- Draw a diagram…

Q: Define nucleation phase

A: given: Define nucleation phase.

Q: Suppose you are asked to manufacture a critical component based on a nickel-based super-alloy. The…

A: GIVEN: Manufacture a critical component based on nickel based super alloy

Q: Is it correct to say Thick pearlite is not as strong as thin pearlite?

A: Thick pearlite is also known as coarse pearlite. And thin pearlite is known as fine pearlite.

Q: An AL disk with a diameter = 10 cm and thickness = 5 cm is cast of pure aluminum in a sand casting…

Q: Translate the given information in your words, figures given below. Time-temperature cooling curve…

A: Cooling Curve: It is a curve that represents the phase of material from gas to liquid or liquid to…

Q: Is this a austenite microstructure if so how can you tell

A: Austenite is in terms of heat treatment of the steel. It is the decomposition of Austenite that is…

Q: What will happen to the points or pattern on a ternary phase diagram if temperature increases or…

A: A ternary phase diagram is a diagram which shows the phase behaviour of a system which consists of…

Q: Explain the concept of zone refining and also explain the refining technique for germanium ingot.

A: Given Germanium ingot To find Zone refining Germanium ingot refining

Q: Describe three types of matrix phase and explain the purpose of dispersed phases on each matrix…

A: The matrix phase is the continuous phase in which a composite alloy is formed in a microstructure of…

Q: As the magnesium content of compacted iron increases, the graphite nodularity.

A: Answer is Increases.

Q: changes llocated alloy Juring age Thardening. You should use a sketch the microstructure of your…

Q: (9,00 Puanlar) A riser in the shape of a sphere is to be designed for a sand casting mold. The…

Q: What is the critical value of G for the directional solidification of two Al-Cu alloys (one…

A: Here, Rate of super conductivity ,v=0.08 mms . Partition coefficient , k=0.14. m=-2.6°Cwt%.…

Q: i need the answer to this question please not the composition : Discuss the indicators of…

A: As shown in the drawing the following weight percentage and the composition of Bismuth and Tin are…

Q: Discuss two property types to consider when selecting a material to process the following product…

A: To be discussed : material property selection for Industrial Robotic Manipulator Bicycle Frame

Q: One of the most common production techniques for metallic implants is lost-wax casting. Discuss the…

A: Lost wax casting, also known as investment casting is a casting process that makes use of wax…

Q: Calculate the degrees of freedom for Points 1-4

A: Gibbs Phase rules - F= C-P+2 where F is the degrees of freedom C is number of components P is the…

Q: Compute the volume percent of graphite VGr in a 3.3 wt% C cast iron, assuming that all the carbon…

Q: Materials Science. From picture below.Describe in detail the phase transformations (showing cooling…

A: Solution: Given Data:

Q: How can permeability effect in sand casting operation and how we can plan an experment to see the…

A: In sand-casting operation is one of the oldest operations. In this, the casting is made by using a…

Q: Problem 1 Suppose we want to cast a magnesium bar 20x20x45 mm³. We are to use a mid gating (exactly…

A: Given: The casting volume, V = 20x20x45 mm3 The diameter to height ratio of the riser, D/H = 1/1.2…

Q: At longer annealing times at appropriate temperatures, larger grains consume smaller ones. Summerize…

A: Annealing - Annealing is a heat treatment process generally use for steel structures. In annealing…

Q: 2) The region showing planar growth during solidification near the fusion zone boundary will exhibit…

Q: For an engine casing casting, would you select: 1000 C y (austentite) a +Y y + cementite a + Fe,C…

A: Answer:- Fe-3.5%C steel

Q: Is it possible to manufacture a propeller of a commercial-scale heavy-duty ship using the Investment…

A: The investment casting process is a special casting process in which the pattern made up of wax or…

Q: Briefly describe the phenomenon of coring (also known as segregation) that occurs during…

A: Given question is related to material science.

Q: An eutectoid steel is cooled slowly from 1000 °C to room temperature by the following different…

A: When eutectoid steel is at 1000 °C it is in - austenite form. - Austenite form is the interstitial…

Q: b) For the solidification of a metal, Tm =1000K with undercooling of 200K, calculate the rate of…

A: Given, Tm=1000 K∆T=200 K Vibration frequency, ν=1012/s Enthalpy change on solidification per unit…

Q: QI/ Explain with drawing the Time- Temperature- Transformation (TTT) diagram?

A: TTT Diagram :- Note :- you have posted multiple questions on single window. As per the…

Q: if u have a variety of materials including low carbon steel, cast iron, high carbon steel, aluminum…

A: Concept: 1) Formability: It is the property of material that upon applying force the material can be…

Q: Please use phase diagram to explain why micro-segregation and macro-segregation happen during…

A: Solidification is basically a phenomenon that plays a great role in developing the diverse…

Q: Describe the process conditions necessary to create a)a cored microstructure

Q: Question a Clood weting of the solid by the liquid is a fundameotal tequirement for hiquid phase…

A: Given data:

Q: Heterogeneous nucleation requires (larger / smaller) supercooling than homogeneous nucleation.

A: Given data:- Heterogeneous nucleation and homogeneous nucleation. To be explained:-Heterogeneous…

Concept explainers

Metal Casting

Metal casting is described as a manufacturing process in which a mold cavity is produced by sand, and molten metal is filled inside a mold cavity. The desirable shaped object is achieved after the solidification of molten metal. Large metal objects like machine beds, motor bodies, and others can easily be manufactured using metal casting. The place or shop where metal casting is performed is called foundry.

Question

100%

What is the microstructure seen in the sem images of ASTM A128 (high manganease casting)

x100
20.0kV LED
100μm Guest
2023/04/24
WD 10.0mm 13:54:05
SEM

x1,000
20.0kV LED
10μm
SEM
Guest
2023/04/24
WD 10.0mm 13:44:05

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: first image

VIEW

Step 2: second image

VIEW

Solution

VIEW

Step by step

Solved in 3 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Nickel-based alloys are used for gas turbine blades in aerospace engines. Briefly discuss the characteristics that make these alloys the choice for this application. Single-crystal technology is applied to nickel alloys that are used as gas turbine blades in aerospace engines. With the aid of sketches describe how a single-crystal casting can be manufactured and explain why a single-crystal casting is likely to have superior creep resistance than a directly-solidified one. Demonstrate the application of the Ten-percent Rule by calculating the approximate tensile strength and elastic modulus in the 0° direction of a carbon-fibre reinforced polymer composite if the strength and elastic moduluş in the 0° single ply are 3620 MPa and 143 GPa respectively. The lay-up sequence of the composite is [02/+45/-45/902]s.
What is pressure die casting? Explain the six major steps in pressure die casting process with neat diagram and indicate all the parts of it.
Why are aluminum and copper alloys unsuitable for use in hot chamber die casting
Explain two important differences between martensitic and pearlitic transformations.
8) The figure schematically shows the solidification stages of an ingot. What would you call the dark region in this image and what would you do to reduce its dent? cm
At what temperature does solidification form at 10% Ni? T(°C) 1600 1500 1400 1300 1200 1100 1000, Answer: L (liquid) L+a solidus liquidus 20 40 60 wt% Ni 86 100
Describe three types of matrix phase and explain the purpose of disbursed phases on each matrix phase.
On the continuous growth, Calculate the interfacial undercooling if the melting temperature is 600 K and the latent heat of melting is given as 30 kJ/kg? (Assume the driving force for solidification as 45 kJ/kg?
ADVANCED MANUFACTURING PROCESS Outline the advanced casting process that would be most suitable for making total knee replacement that required high dimensional accuracy.Choose one biomedical grade alloy used to make total knee replacement. Explain your choices with details justification.
Which of these factors causes more porosity to form toward the interior of a casting rather than toward the outside? (a) Gasses are less soluble in the solid metal than the liquid, so solidified areas push dissolved gasses toward the interior. (b) Casting under a vacuum causes gasses near the liquid metal surface to be drawn out of the liquid during solidification. (c) The feeding structures of the mold are designed to force entrapped air into the center of the casting. (d) Draft on the mold wall forces air bubbles toward the interior of the solidifying metal. (e) None of the above Non-eutectic alloys (most commercial alloys) solidify over a temperature range. Which of the following statements explains how this affects the casting process. (a) Solidified non-eutectic alloys are especially difficult to remove from metal dies (b) Non-eutectic alloys have significantly less fluidity than pure metals or eutectic alloys. (c) Non-eutectic alloys solidify starting from the outside of the…
what solidification time is required for a casting of 9.5 cm3 and a mold contact area of 10 cm2? The mold constant is 838 s/cm2.