The stress-strain data from a tensile test on a cast-iron specimen are e (10-3) O (kpsi) 0.20 0.44 0.80 1.0 1.5 2.0 2.8 3.4 4.0 5.0 10 16 19 26 32 40 46 49 54 NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part. ermine the tangent modulus, E, at a value of o = 0 psi. tangent modulus, E is 106 psi.

The stress-strain data from a tensile test on a cast-iron specimen are e (10-3) O (kpsi) 0.20 0.44 0.80 1.0 1.5 2.0 2.8 3.4 4.0 5.0 10 16 19 26 32 40 46 49 54 NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part. ermine the tangent modulus, E, at a value of o = 0 psi. tangent modulus, E is 106 psi.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: /Wmsthe value of angle 0f andthevetueof02 -1000N

A: Calculated angles theta 1 and theta 2 .

Q: hi still waiting on the last part of the question..

A: Application of ballast tanks in aerospace

Q: Write the four different types of Resultant Loadings?

A: Loading: The loading on the beam or any members is the load acting on a beam under which beam…

Q: 3

Q: 2. Determine the reading on the vernier scale as indicated by the arrows. 25 30 35 40 10 20 30 40 50…

A: Least count of Vernier caliper = 0.02 mm

Q: can you answer 1B

Q: In the diagram below, particle P travels along the curved guide due to the counterclockwise rotation…

Q: -150 mm 15 mm B C 150 mm -15 mm 15 mm - 100 mm·

A: given;

Q: (b) 1489.5m³ (C) 128

A: given:bore diameter d=68mmstroke length l=75mm

Q: B A

A: Given that , m =3 kg t=0.35 s r=4 sin3θ

Q: What is the moment's function?

A: Moment deals with the physical quantities situated at some distance relative to the reference point.…

Q: G Determine the equillalent. tiffness for the dreegreem

A: Solution:

Q: (-6).(-4) – 3(-5) 11-기-12+ (-5)|

Q: The answers should not be in vector form. Please re-anser. Rate will be given

Q: Q3/ For the plate shown in figure below find * (a) ΣΑ YA 7 9. X 8 5

Q: A differential element on the bracket as shown in Figure Q1 is subjected to plane strain that has…

Q: 5と 2' 111ド 7K 8'一 16- 251

Q: M, B

A: Given data, The reaction at A and B can be calculated as -

Q: At a given moment four link mechanism OABO, is in the position shown on the figure and OA= AB = AO =…

Q: part ii

Q: (b) Find the natural frequencies and mode shapes. (c) Calculate the natural frequencies and mode…

Q: 19) During the Vicker harness experiment, it is found that the diameter of indenter is larger than…

Q: The 10-kg crate is subjected to a force having a constant direction and a magnitude F = 100 N. When…

Question

The stress-strain data from a tensile test on a cast-iron specimen are
E (10-3)
O (kpsi)
0.20
0.44
0.80
1.0
1.5
2.0
2.8
3.4
4.0
5.0
15
10
16
19
26
32
40
46
49
54
NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part.
Determine the tangent modulus, E, at a value of o = 0 psi.
The tangent modulus, E is
106 psi.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

The data illustrated below have been determined while the tension test of the stainless steel sample by amateur engineers. The gage length of the stainless steel sample was 50.8 mm (2.0in.) and, the original diameter of the steel sample was 12.8 mm (0.505in.). Load (Ib) Elongation (in.) Load (Ib) Elongation (in.) 14000 0.020 2 310 0.0022 14400 0.025 4 640 0.0044 14 500 0.060 6950 0.0066 14600 0.080 9 290 0.0088 14800 0.100 11 600 0.0110 14 600 0.120 13000 0.0150 13600 Fracture With the help of Excel, plot the stress-strain diagram for this test conducted, and define the following mechanical properties: a) Young modulus; b) Proportional limit; c) Yield stress @0.2% offset; d) ultimate stress; e) nominal rupture stress.
A tensile test was performed on a metal specimen with a diameter of 1/2 inch and a gage length (the length over which the elongation is meas- ured) of 4 inches. The data were plotted on a load-displacement graph, P vs. AL. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/AL = 1392 kips/in. What is the modulus of elasticity? BI
3
A high-impulse universal testing machine is being used to determine the Young's Modulus of a rectangular solid specimen (l = 20 cm, t = 1.5 cm, w = 2 cm). The machine produces 35,000 Ns that causes the impact force of compression resulted to a 1 mm deformation in the length of the specimen in 0.05 s. Determine the Young's modulus of the specimen expressed in MPa. Round off your answer to the nearest whole number
Please show handwritten solution
The stress-strain data from a tensile test on a cast-iron specimen are € (10-3) 0 0.20 0.44 0.80 1.0 1.5 2.0 26 32 40 46 49 54 NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part. 2.8 3.4 4.0 5.0 a (kpsi) 0 5 10 16 19 Determine the tangent modulus, E, at a value of a=0 psi. 106 psl. The tangent modulus, Eis X
The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
1. A tension test on an aluminum plate resulted in the following engineering stress-engineering strain data as reported in the first and second column of the table below (reduction of area, RA=17%): S (psi) e (in/in) σ (psi) ε (in/in) 10500 0.001 10510.5 0.000995 21000 0.002 31200 0.003 41300 0.004 51200 0.005 61200 0.006 70600 0.007 74700 0.0075 76800 0.008 77600 0.0085 78000 0.009 78400 0.0095 78700 0.01 81200 0.02 83000 0.03 84200 0.04 85400 0.05 86200 0.06 86800 0.07 *87200 0.08 **86200 0.1 Note: * maximum load, ** load at fracture a) Calculate the corresponding true stress and true strain and give your results in a table along with the engineering stress, engineering strain shown in the of table above (column 3 and 4). b) Plot the true stress-true strain curve on a rectangular coordinate. c) Plot the true stress-true strain curve on a log-log graph and determine the plastic flow curve parameters K and n, the yield strength, Y, and the elastic modulus, E of the material.
The following data were recorded during the tensile test of a test specimen with a diameter of 12.8 mm. The gage length is 50.8 mm. The given data are as follow; Given: Test specimen material: Aluminum Diameter of test specimen: Do = 12.8 mm Length of test specimen: Lo = 50.8 mm Force and Elongation data for test specimen Assumptions: 1. The given data is accurate and the material is isotropic 2. The direction of applied force is parallel to the length of the cylinder Requirement: To interpret and plot the stress Vs Strain curve for a given specimen DATA: LENGTH, mm STRESS, MPa LOAD, N 0 50.8 7 330 50.851 15 100 50.902 23 100 50.952 30 400 51.003 34 400 51.054 38 400 51.308 41 300 51.816 44 800 52.832 46 200 53.848 47 300 54.864 47 500 55.88 36 100 56.896 44 800 57.658 42 600 58.42 36 400 59.182 STRAIN
In a tensile test of stainless steel, the following data were obtained: Load (N) 7,200 11,250 13.500 16,200 18.900 Elongation (mm) 0.0 0.505 2.03 5.08 20,200 15.24 20,700 13,200 24.90 10.16 21.80 The dimensions of the cylindrical specimen were initial length L₁ = 50.8 mm and initial arca A₁ - 35.8 mm² and the area at fracture was Ar 10.0 mm². Plot the stress-strain diagram and determine the following: a) Modulus of elasticity b) The yield strength at a strain offset of 0.002 c) Ultimate strength d) Fracture strength
1. A tensile test was conducted on a metal "505" specimen and the following stress-strain curves were generated, both curves generated from the same set of data. Use the graphs to fill in the mechanical properties of the material tested in the box below. Don't forget units! Stress vs Strain Stress, psi Stress, psi 80000 70000 60000 50000 40000 30000 20000 10000 0 0.00 80000 70000 60000 50000 40000 30000 20000 10000 0.02 0 0.000 0.002 0.04 0.004 0.06 0.006 0.08 0.10 Strain Stress vs Strain 0.008 0.12 Elastic Modulus, E: 0.2% Offset Yield Strength, oo: Tensile Strength, ou: Breaking Strength, of: % Elongation: 0.14 0.010 0.012 0.014 Strain 0.16 0.18 0.016 0.018 0.20 0.020
Q1- The following data was obtained tensile test ɔn a specimen of 10 mm diameter and gauge length Lo=50 mm: 0 38 | 76.2 92.7 107 149 160.4 | 155 142 124.7 load(KN) | elongation(mm) 0 0.02 0.12 0.25 0.50 2.03 3.55 4.06 5.1 5.84 Using the graphic paper supplied, Plot engineering stress-strain curves, then determine the (ay, ey), (ou , eu), (of,, ef), modulus of elasticity, then detected in the draw ((stroin hardening (m)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region))?