The following stresses were measured for a specimen: 011 = 94 MPa; 022 = 155 MPa; ơ12 = 85 MPa Determine whether not yielding occurred using both the Tresca and von Mises criteria, given that oys = 180 MPa. Which criterion is more conservative?

The following stresses were measured for a specimen: 011 = 94 MPa; 022 = 155 MPa; ơ12 = 85 MPa Determine whether not yielding occurred using both the Tresca and von Mises criteria, given that oys = 180 MPa. Which criterion is more conservative?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: During testing of cast iron in compression, the original diameter of 2 inches was increased by…

A: Stress = Force/Area

Q: Q2) Based on data below, draw the S-N curve for fatigue test if the specimen have neck diameter 5mm,…

A: Write the formula for the maximum stress at the neck. S=32PLπd3 Here, S is the maximum stress, P is…

Q: Q1. A ductile hot-rolled steel bar has a minimum yield strength in tension and compression of 350…

A: A ductile hot-rolled steel bar has a minimum yield strength in tension and compression of Syt= 350…

Q: Consider the plates shown in (Figure 1). Take P18 kip and P₂ -9 kip. Determine the maximum average…

Q: Examine the stress-strain curves below and choose the correct statement from B the ones listed…

A: Material A is showing brittle plastic behaviour, Material B is showing toughness and strong plastic…

Q: A machine component is modeled as a solid round cross section rod with two loads. At the location of…

A: Axial forceTorqueDiameterLength

Q: A tensile test for a copper specimen has been performed and the following data are obtained. -…

A: Given data: The percentage of elongation, %L = 60%. The percentage of reduction in area, %A = 36%.…

Q: Material A, has a yield strength of 902.88 MPa (125,000psi) and a plane strain fracture toughness of…

A: Given data as per question yield strength=902.88 Mpaplane strain fracture toughness=100.16 MpaSize…

Q: Q/1_prove that true stress Ở True = O Eng (1+ €Eng) 2- prove that true strain ETrue = In(1+ EEng),…

A: TO PROVE :- σtrue=σeng(1+εeng)εtrue=ln(1+εeng)

Q: Using reflective symmetry, determine the maximum deformation and the maximum normal stress that the…

A: Given:- Size of plate : 2 inch in height and 0.25 inch in width hole diameter : .75 inch

Q: What type of behaviour is observed from these stress-strain curves?

A: Consider the diagram shown below for the stress-strain curve. P: proportional limit Y: yield point…

Q: An machine part is being tested with a load of 63,000 lb. The allowable tensile stress is 10,000…

A: Given : load (P) = 63000 lb allowable tensile stress = 10000 psi factor of safety = 3 original…

Q: The aluminum shell is fully bonded to the brass core, and the assembly is unstressed at a…

Q: Question 3: A specimen having a circular section (D. = 30 mm, t = 1 mm) and length, L = 200 mm is…

A: According to the given data L=200mm T=30N-m θ=60π180=1.047 rad Do=30mm t=1mm We need to find…

Q: The following data are obtained from a tensile test of a copper specimen. - The load at the yield…

A: 1 MPa= 1N/mm2

Q: A tensile test for a copper specimen has been performed and the following data are obtained. -…

A: Answer 1: Elongation = 69% Final length = 35.5 mm Calculate the initial length by using the unitary…

Q: Nominal or engineering strain in the rod

A: Given DataThe gauge length of the specimen The initial diameter d0 =0.5 inYield stress f…

Q: Choose correct answer: The linear strain is opposite to ----------------------------------------…

A: This question is from strength of material.

Q: 2. Mild Steel is tested in the laboratory. The data obtained are: Length of Specimen = 320 mm/…

A: Given Data: Length of specimen L1=320 mm Diameter of Specimen d=30 mm Load F=20 kN Elongation under…

Q: .. An machine part is being tested with a load of 63,000 lb. The allowable tensile stress is 10,000…

A: Given:Allowable Tensile Stress on machine=σmaximum=10000 psi(pound per square…

Q: Suppose you need to design a tension test machine capable of testing specimens that have nominal…

Q: If the area under the stress and strain curve is less then it is concluded that the material has low…

A: The area under stress and strain curve represent the toughness of the specimen material.

Q: Determine the smallest yield stress for steel that might be selected for the part, based on the…

A: Given data,the state of stressFind outthe smallest yield stress for steel using the maximum shear…

Q: A titanium alloy (Ti-5Al-2.5Sn) specimen with the dimensions shown below is subjected to a uniaxial…

A: The stress of a bar is given by, , where P is the normal load and A is the cross-section area of…

Q: A specimen with an initial diameter of 12 + b* was tested under tensile conditions and a maximum…

A: Given Data : Maximum loadFmax=60 KN Strain recorded when applied maximum load ε1=65%=65100=0.65…

Q: Q1. A typical graph of strain (e) versus time for a metal under creep conditions is shown below. င်…

A: DISCLAIMER FOR MULTIPLE Since you have asked multiple question, we will solve the first question for…

Q: 0.09. Assuming that a A metal has a strength coefficient K = 210,000 psi and n tensile-test specimen…

A: find true UTS Detailed calculation is provided in solution part

Q: A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of…

Q: Which of the following could not be obtained directly from the stress-strain diagram from a tensile…

A: Draw stress - strain diagram and find which property from the following is not obtained from the…

Q: CALCULATIONS 4.1 Using the given pulley radius and the weight values, calculate the torque applied…

A: Disclaimer: Since you have posted a question with multiple sub-parts, we will solve first three sub…

Q: Part B The stress-strain dagram for a steel aloy having an original diameter of 1.0 in. and a gage…

Q: Determine the maximum axial force P that can be applied so as not to exceed an allowable tensile…

Q: Use the Mohr's circle to determine average normal strain. AΣo↓vec ΑΣΦ Eavg= ?

Q: I Review Express your answer to three significant figures and include appropriate units. The rod has…

A: find the shear stress at point B

Q: A mild steel tensile specimen of initial length 44 mm and initial diameter 6.4 mm is subjected to a…

A: To find (a) The fracture load F. (b) The final length l'. (c) The final area Af. Given The initial…

Q: i) Initial Length (in mm) = Answer for part 1 ii) Final Area (in mm2) = Answer for part 2 iii)…

Q: A brass specimen is subjected to a Tensile test in a laboratory. The following data obtained are:…

Q: A bronze alloy specimen having a diameter of 12.8 mm and a gage length of 50 mm was tested to…

Q: 39)A tensile test specimen has a gage length=3.0 inches and a diameter= .75 inches. Yielding occurs…

A: Given:

Q: For some metal alloy, a true stress 345 MPa (50040 psi) produces a plastic true strain of 0.02. How…

A: True stress, = 345 MPaTrue plastic strain = 0.02New true stress = 418 MPaOriginal length, lo = 500…

Q: A tensile test for a copper specimen has been performed and the following data are obtained. -…

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

The following stresses were measured for a specimen:
011 = 94 MPa; 022 = 155 MPa; ơ12 = 85 MPa
Determine whether not yielding occurred using both the Tresca and von
Mises criteria, given that oys = 180 MPa. Which criterion is more
conservative?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Whats the correct answer for this please ?
Annealed low-carbon steel has a flow curve with strength coefficient = 80,000 lb/in2 and strain-hardening exponent = 0.25. A tensile test specimen with gage length = 2.0 in is stretched to a length = 3.5 in. Determine the flow stress and average flow stress that the metal experienced during this deformation. use correct stratgy and correct E 0.55962
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 147 kN. - Length of the specimen is 28 mm. - The yield strength is 75 kN/mm2. - The percentage of elongation is 49 %. Determine the following iii) Stress under an elastic load of 16 kN, iv) Young's Modulus if the elongation is 1 mm at 16 kN and (v) Final diameter if the percentage of reduction in area is 22 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
Find tensile load
Q: Choose the correct answer: 1- The true stress of metallic sample which was subject to the mechanical test is equal to which of the following values?? If you know that the sample radius before and after the fracture are (6.3mm) and (0.2in.) respectively, and the failure occurs at (65*10 psi)? 660MPA, 680.03 10ʻPa, 689.04 10’KPa, 710 10ʻPa
Correctly solve by using correct expression
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 66 % - Percentage of Reduction in Area = 38 % - Final length after fracture = 34.6 mm - Final Diameter after fracture = 4.43 mm & - Ultimate stress = 364 MPa Determine the Initial length, Initial diameter and Maximum load. ii) Final Area (in mm2) = iii) Initial Area (in mm2) =
1- The ultimate tensile strength of metallic sample is equal to which of the following values? If that the initial and final radius are (0.256in.) and (0.157in.) respectively. The failure occurs at maximum weight of (84*10 gm)? What is behavior type of sample? 559*10 (N/m2), as brittle behavior 620*10 (N/m2), as brittle behavior 620*10(N/m?), as ductile behavior 560MPA, as brittle behavior
Determine the factor of safety as per tresca's max shear stress theory
The table below shows the deformation data that resulted from applying a pure tensile load to a brass alloy rod with an initial length of 30 mm and a diameter of 10 mm. This rod was subjected to necking and beyond necking deformation. The data at fracture is shown in the last row. Applied Load (N) Length (mm) Diameter (mm) 75,100 33.8 68, 250 34.9 50,200 35.7 6.7 Solve for the TRUE STRESS/ES and TRUE STRAINS. 8.3 7.8
M 1:-A O photo_2021-02-1.. -> 200 stress 150 (MPa) L00 50 0.1 0-2 strain From the tensile stress-strain behavior fer the brass specimen the foibuding:- O the diameter is 12-8 mm Calcalate 1- The Yield stress. 2- Modulus of elasticity. 3 - The Tensile strength . II
What is the true answer