HW1The following data were obtained from a tensile test on a specimen of10 mm diameter and gauge length 60mm , the diameter after fracture was7mm . Using the graph paper supplied, plot the load-extension diagram andthen1- Plot the data as engineering stress versus engineering strain.2- Determine Young Modulus3- Determine the yield strength at a strain offset of 0.002.4- Determine maximum tensile strength of this alloy.5- What is the approximate ductility?Load (kN)Extension (mm) | 0.2132 | 142140 1358.5 10.0 12.016325672951100.40.70.91.52.55.0

Answered: Image /qna-images/answer/843417e2-3feb-4673-8522-e7c9a5f0ad5a.jpg

The following data were obtained from a tensile test on a specimen of 10 mm diameter and gauge length 60mm , the diameter after fracture was 7mm . Using the graph paper supplied, plot the load-extension diagram and then

The following data were obtained from a tensile test on a specimen of 10 mm diameter and gauge length 60mm , the diameter after fracture was 7mm . Using the graph paper supplied, plot the load-extension diagram and then

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A material has a linear elastic perfectly plastic stress-strain. A cylindrical specimen of that material having an initial length of 35 mm and a tadius of 7 mm is pulled until it elongates 0.8mm. a. Calculate the stain and the corresponding stress at that elongation value. b. Afterward, the specimen is released to zero stress level, how does the final length of the specimen compare with its original length? How much plastic deformation remains if it exists?
A mild steel tensile specimen of initial length 44 mm and initial diameter 6.4 mm is subjected to a tensile test and the following data are obtained. - Yield Strength as 88 MPa - Maximum Strength as 212 MPa - Fracture Strength as 152 MPa - Percentage of Elongation as 63 % - Percentage of Reduction in area as 39% Determine the Fracture load The Final length in mm = The Final area in mm2 =
1. For the stress-strain curve shown below, please estimate the properties indicated. (a) Fracture Strain Please do your work on a separate sheet of paper, and put your answers in the boxes on the right. Be sure to include the proper symbol and units. Stress Strain 70 60 50 Stress (ksi) 240 30 20 10 70 0 0.000 60 50 Stress (ksi) 40 20 10 KULL 0 0.000 0.010 0.050 0.100 Strain (in/in) Stress Strain 0.020 0.030 Strain (in/in) 0.040 0.150 0.050 (b) Ultimate Tensile Stress (c) Fracture Stress (d) Proportional Limit (e) Elastic Modulus (1) Yield Stress (g) Tensile Toughness (Modulus of Toughness) (h) Modulus of Resilience
In the Table below Data for Mar M 247-a Nickel base superalloy is shown. (1) Plot the steady state strain rate and time to rupture to predict a relationship between the two variables. Provide an equation for the relationship that you see. (2) Give an explanation as to why the fracture elongation is going up with stress.
A tension test was conducted for a cylindrical specimen of stain-less steel having an initial diameter (D) of 15.35 mm. Calculate the percentage reduction in area if the fracture diameter of the specimen (d) is 10.25 mm. Select one: O a. 55.41% O b. 56.41% O c. 57.41% O d. 58.41%
Attempt only if you are sure Urgent.
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 66 % - Percentage of Reduction in Area = 38 % - Final length after fracture = 34.6 mm - Final Diameter after fracture = 4.43 mm & - Ultimate stress = 364 1) Final Area (in mm2) = 2) Initial Area (in mm2) = 3) Ultimate Load (in N) =
A tension test was conducted for a cylindrical specimen of stain-less steel having an initial diameter (D) of 10.85 mm. Calculate the percentage reduction in area if the fracture diameter of the specimen (d) is 6.15 mm. Select one: O a. 68.87% O b. 69.87% c. 66.87% O d. 67.87%
I need the answer as soon as possible
the creep data for two different samples. You have been asked to analyse the results, if you know that the original length of specimen is 17.4625 mm and the original width is 4.8 mm and the original thickness 1.6 mm and the cross sectional area is 7.68 mm: 1. Compare the lifetime for these samples.2. Determine the rapture lifetime for the samples below. 3. Calculate the creep rate for all of them
(b) A 12.8 mm diameter rod and gauge length of 40 mm of aluminum alloy is pulled to failure in a tensile test. If final diameter of the rod fracture surface is 10.8 mm and fracture gauge is 64 mm, answer the following: (i) Calculate the ductility in percent reduction in area of the sample. (ii) Explain how ductility is related to the toughness of the material.
3. A rod-shaped MgO specimen with round cross section is tested with the three-point bend method. What is the calculated minimum radius without fracture if the applied load is 5560 N, the flexural strength is 105 MPa, and the separation between the two support pins is 45 mm?