The Fe-C phase diagram is given: How much of the Primary phase for a Fe-0.55% C alloy forms at500°C? What is the weight fraction of the total cementite for the same alloy at 500°C?Composition (at% C)51015202516001538°C1493°CL140025001394°Cy+L12001147°C2.144.30Y, Austenite20001000912°Cy+ Fe3C8001500727°C0.760.022600`a, Ferritea + Fe3CCementite (Fe3C)1000400146.6.70(Fe)Composition (wt% C)Temperature (°C)Temperature (°F)

Answered: Image /qna-images/answer/4465ef4b-fb95-476c-8831-c62eccbecd0b.jpg

Answered: The Fe-C phase diagram is given: How…

The Fe-C phase diagram is given: How much of the Primary phase for a Fe-0.55% C alloy forms at 500°C? What is the weight fraction of the total cementite for the same alloy at 500°C?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Consider 2.4 kg of a 99.7 wt% Fe-0.3 wt% C alloy that is cooled to a temperature just below the…

Q: 700 L 600 500- (A1)+ (A1)+ O 400 (A1) emperature,

A: steps :- (1) solutioning (2) quenching (3) aging Maximum hardness will be obtained at an optimum…

Q: Compute the mass fractions of a ferrite and cementite in pearlite. Assume T 726 C°. W₁ = WFe3 C i =

A: Given: T = 726 C To find the mass fraction of α ferrite and cementite in Pearlite

Q: Copper-Nickel alloy is widely applied in industry. (a) List at least three applications where Cu-Ni…

A: Given: The wt% of mixture = 40 Wt% CO and 60 Wt% Ni The temperature, T = 1320oC

Q: Consider 4 Kg of a 98.70 wt % Fe, 1.30 wt % C alloy at temperature just below eutectoid, determine…

Q: Sketch a phase diagram for two soluble components. Show the melting tem-perature of each element.…

A: The simplest type of phase diagram for any system can be of two components that are soluble in both…

Q: In the Ni-base superalloys used to make turbine blades, which of the following statements are true?…

A: Options a, b, c, are correct.

Q: Question 5 (12 marks) Referring to the Fe-C phase diagram given below, suppose an austenite having a…

A: The iron-carbon diagram shows the changes in phases of Fe-C at different temperatures as the weight…

Q: .For a steel alloy with .3% carbon, what would the percent of each phase be at 730°C and 725°C?

A: Let us consider a portion of Iron-Carbon diagram as shown below, For the 730 °C and 0.3% of carbon,…

Q: (°C) (liquid) L A

Q: A 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the…

Q: (Q.3) For 30 wt% Cu-70 wt% Ag alloy at 650 "C, (a) what phases are present? (b) What are the…

Q: Q3: A: 40 wt% Sn-60 wt% Pb alloy at 220°C, determine the phases present?

Q: A 1.05% C steel is slowly cooled from 900 °C to temperature just slightly above 723 °C. Calculate…

A: From the iron-carbide diagram understand that γ is used for austenite and Fe3C for cementite. Draw…

Q: Please help

A: Step 1: MgO-65 wt% FeO system:1. Liquidus Temperature: - The liquidus temperature is the…

Q: Temperature = Temperature = Composition (at% Sn) 20 40 60 80 100 327 °C 600 300 Liquid 500 Liquid a…

Q: a. Determine the composition of phases. b. Calculate the amount of phases present in terms of (i)…

Q: ent, of an alloy that consists

A: Atomic% of Cu =5% Atomic% of Pt= 95 % Required Wt% of above elements in alloys

Q: For a 50-50 Mg-Pb alloy, what would the percent of each phase be at 500°C, 300°C and 100°C?

A: Consider the diagram as shown below Given compositions by weight are as,

Q: A hypo-eutectoid steel sample has a mass of 538kg and a nominal carbon content of 0.57%. Sketch the…

A: From the given data,

Q: 5. For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, ii. Calculate the…

Q: 4. The figure below shows the phase diagram for a hypereutectoid plain carbon steel. Assume that…

A: To find:i. The structure at points a, b, c, and d on the diagram.ii. The of proeutectoid ferrite at…

Q: a) A 10g ball bearing sphere is made of a steel containing 2.0 wt% C. Suppose the ball is…

Q: 5

A: A refractory material, often known as a refractory, is a material that resists breakdown caused…

Q: 10 Cite the phases that are present and the phase- Ocompositions for the following alloy (g) 21.7…

Q: a. Determine the composition of each phase in a Cu-40% Ni alloy at 1300°C, 1270°C, 1250°C, and…

A: a. Determine the composition of each phase in a Cu-40% Ni alloy at 1300°C, 1270°C, 1250°C, and…

Q: Draw Iron - Iron Carbide Phase diagram and show the following: 4- Types of ferrous alloys on…

A: given; iron-iron carbide phase diagram;

Q: i need the answer to this question please not the composition : Discuss the indicators of…

A: As shown in the drawing the following weight percentage and the composition of Bismuth and Tin are…

Q: What is a peritectic phase diagram? Draw a typical equilibrium diagram for a eutectic type of system…

A: To explain: The peritectic phase diagram and eutectic system. Concept used: Peritectic phase…

Q: Temperature C For the phase diagram shown calculate the amount of austenite present at the point P…

A: For solution refer below images.

Q: 10-51 Determine the phases present, the compo- sitions of each phase, and the amount of each phase…

Q: lowly cooled plain carbon steel has proeutectoid ferrite to be 10 wt% of its eutectoid ferrite. What…

A: given: Slowly cooled plain carbon steel has proeutectoid ferrite to be 10 wt% of its eutectoid…

Q: What is the crystal structure of martensite? Why can you not find a martensite phase region in the…

A: The crystal structure of the martensite is Body-Centered Tetragonal (BCT). It is a Body-Centered…

Q: he Iron-Carbon system: Phase Diagram 1. You heat treated a 1045 steel plate by heating it to 900°C…

A: The phase diagram is used to predict the microstructure behavior and composition of the…

Q: 10-51 Determine the phases present, the compo- sitions of each phase, and the amount of each phase…

Q: At longer annealing times at appropriate temperatures, larger grains consume smaller ones. Summerize…

A: Annealing - Annealing is a heat treatment process generally use for steel structures. In annealing…

Q: Cite the phases that are present and the phase compositions for the following alloys: 15 wt% Sn–85…

A: The allot properties- 15 wt% Sn–85 wt% P The temperature,T =100°C To find: The phases and the…

Q: Draw Fe-C binary phase diagram and compute percentage of the phases in eutectoid steel.

Q: According to the following graph, two samples of 1080 steel are cooled from the eutectoid…

A: Given: To find: Formation and microstructure

Q: To increase the hardness of a steel gear, it was carburized at 850oC by introducing 1.3%C at its…

A: 0.6754%Explanation:

Q: Specify all temperature-compositicn points at which eutectics, eutectoids and peritectics. At 700…

A: Redraw the given phase diagram.

Q: Describe experimental procedure to obtain a binary isomorphic phase diagram for metals A and B by…

Q: (a) Calculate the wt% of Ni and Cu. (b) Based on the figure below, what is the tensile strength of…

A: Given data:NiCu barThe bar has a 0.01 m x 0.01m cross-section and is 1m longThe alloy is 60% (wt%)…

Question

The Fe-C phase diagram is given: How much of the Primary phase for a Fe-0.55% C alloy forms at
500°C? What is the weight fraction of the total cementite for the same alloy at 500°C?
Composition (at% C)
5
10
15
20
25
1600
1538°C
1493°C
L
1400
2500
1394°C
y+L
1200
1147°C
2.14
4.30
Y, Austenite
2000
1000
912°C
y+ Fe3C
800
1500
727°C
0.76
0.022
600
`a, Ferrite
a + Fe3C
Cementite (Fe3C)
1000
400
1
4
6.
6.70
(Fe)
Composition (wt% C)
Temperature (°C)
Temperature (°F)

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Elastic Constants and Their Relationship

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Answer ASAP
For an alloy containing 20 wt % Ag, refer to the Cu-Ag phase diagram given in the Figure: What is the melting point of Cu in °C? What are the relative amounts(in %) of the existing phases at 900°C? Define the Eutectic point in terms of °C and the composition % of Ag.
Determine the fraction of eutectoid cementite with 0.84 wt.% C in the iron-carbon alloy.
What is meant by a phase? Describe an example. And what is the equilibrium phase diagram?
Consider a Fe-0.5% C alloy. What is the amount of pro eutectoid phase (in percentage ) just above the eutectoid temperature
I need neat and clean handwritten solution. Don't give typed solution. Correct answer will be upvoted only.do remember
Correct and complete solution please
the PCS containing 0.4%C was quenched hardened in water, amd tempered at 400oC. sketch and identify the phases of the microstructure pf the stell at rhe following states a) above the upper critical point just before quenching in water b) after quenching I’m water prior to tempering C) after tempering
Material science
Answer part b
For some given binary phase diagram, describe how you would: find the temperatures and compositions of all eutectic, eutectoid, peritectic, and congruent phase transformations write reactions for all these transformations for either heating or cooling (show an example).
A 10 30 70 1) For an A-B alloy of composition 25 wt% B (i) Draw the microstructure at T (just above the eutectoid temperature) and calculate the fraction of each phase in the microstructure. (ii) Draw the microstructure at T (just below the eutectoid temperature) and determine the amount of each phase, i.e., fraction of proeutectoid alpha, eutectoid alpha and eutectoid beta. 2) Provide a brief summary of phase transformations which are often observed in the iron-carbon alloy system due to various heat treatment procedures carried out to tune the microstructure. Compare mechanical strength and ductility of the materials/microstructures that form as a result of such heat treatment processes.