Q1/ Consider the brass alloy for which the stress-strain behavior is shown in the figure below. A cylindrical specimen of this material 10.0 mm in diameter and 101.6 mm long is pulled in tension with a force of 10,000 N. If it is known that this alloy has a value for Poisson's ratio of 0.35, compute (a) the specimen elongation, and (b) the reduction in specimen diameter. 500 70 Tensile strength 450 MPa (65,000 psi) 60 400 50 10 psi 300 MPa 40 40 30 200 Yield strength 30 200 250 MPa (36,000 psi) 100 20 10 100 10 0.005 0.10 0.20 0.30 0.40 Strain Stress (MPa) 20 T Stress (10 psi)

Q1/ Consider the brass alloy for which the stress-strain behavior is shown in the figure below. A cylindrical specimen of this material 10.0 mm in diameter and 101.6 mm long is pulled in tension with a force of 10,000 N. If it is known that this alloy has a value for Poisson's ratio of 0.35, compute (a) the specimen elongation, and (b) the reduction in specimen diameter. 500 70 Tensile strength 450 MPa (65,000 psi) 60 400 50 10 psi 300 MPa 40 40 30 200 Yield strength 30 200 250 MPa (36,000 psi) 100 20 10 100 10 0.005 0.10 0.20 0.30 0.40 Strain Stress (MPa) 20 T Stress (10 psi)

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A cylindrical tensile specimen has an undeformed diameter of 8.6 mm. It is subjected to a tensile load of 100 kN. The elastic modulus (E) is 10 GPa. Poisson's ratio is 0.25. Calculate the change in the diameter (in mm).
The stress-strain diagram for a steel alloy having an original diameter of 0.5 in. and a gage length of 2 in. is given in the figure. If the specimen is loaded until it is stressed to 70 ksi, determine the approximate amount of elastic recovery and the increase in the gage length after it is unloaded. o (ksi) 80 70 60 50 40 30 20 10 e (in./in.) 0 04 0.08 0.12 0.16 0.20 0.24 0.28 0 0005 0.0010.0015 0.002 0.0025 0.0030.0035
The elastic portion of the tension stress-strain diagram for an aluminum alloy is shown in the figure. The specimen used for the test has a gauge length of 2 in. and a diameter of 0.5 in. If the applied load is 10 kip, determine the new diameter of the specimen. The shear modulus is G al =3.811032 ksi
This figure shows typical stress-strain behaviour for a brass. The inset figure shows the behaviour at low strains. 500 70 Tosle strength 450 MPa 166,000 ps 60 400 300 MP 40 30 200 Yeld steg 250 MPa (,0a 200 20아 100- 20 100 10 0.20 030 040 If the cylindrical test sample is initially 14cm long with an initial radius of 2mm, estimate the true stress in MPa at the ultimate tensile stress. (Enter your answer to the nearest whole number) an es
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 800 mm. The cross-sectional dimensions of the beam are b1 = 35 mm, d1 = 108 mm, b2 = 21 mm, d2 = 21 mm, and a = 7 mm. For this material, the allowable tensile bending stress is 20 MPa, and the allowable compressive bending stress is 9 MPa. Determine the largest moment M that can be applied as shown to the beam.
In a tensile test on a metal specimen having a cross section 20 mm by 10 mm elastic breakdown occurred at a load of 70 000 N. A thin plate madec from the same material is to be subjected to loading such that at a certain point in the plate the stresses are o,=-70 N/mm², 7.y= 60 N/mm² and o. Determine the maximum allowable values of o, using the Tresca and von Mises theories of elastic breakdown. Ans. 259 N/mm² (Tresca), 294 N/mm² (von Mises).
A structural component in the shape of a flat plate 24.3 mm thick is to be fabricated from a metal alloy for which the yield strength and plane strain fracture toughness values are 533 MPa and 22.0 MPa-m1/2, respectively. For this particular geometry, the value of Y is 1.3. Assuming a design stress of 0.4 times the yield strength, calculate the critical length of a surface flaw. What formulas do i use ? And how do i use them?
The composite bar of neglible mass is connected to two rods as shown in the figure. If the system is initially free, determine the temperature change that will cause a tensile stress of 60 Mpa in the steel rod.
An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 680 mm. The cross-sectional dimensions of the beam are b, = 36 mm, d1 = 95 mm, b2 = 22 mm, d2 = 22 mm, and a = 7 mm. For this material, the allowable tensile bending stress is 11 MPa, and the allowable compressive bending stress is 13 MPa. Determine the largest moment M that can be applied as shown to the beam. b2 M d2 d1 |A В b1 Answer: M = N-m
Consider a cylindrical specimen of a steel alloy (Please see the figure) 0.33 in. in diameter and 3.15 inches long that is pulled in tension. given:-Elongation is 0.018 in-Tensile stress = 200 ksi -Tensile strain = 6.83*10^-3 -Ultimate stress = 281.82 ksi -Ultimate strain = 0.05solve: Fracture point (stress and strain values)
A cylindrical metal specimen 12.7 mm (0.5 in.) in diameter and 250 mm (10 in.) long is to be subjected to a tensile stress of 28 MPa (4000 psi); at this stress level, the resulting deformation will be totally elastic. (a) If the elongation must be less than 0.080 mm (3.2 x 10-3 in.), which of the metals in Table 6.1 are suitable candidates? O Steel O Nickel Brass O Magnesium O Aluminum O Copper O Titanium O Tungsten (b) If, in addition, the maximum permissible diameter decrease is 1.2 x 103 mm (4.7 × 105 in.) when the tensile stress of 28 MPa is applied, which of the metals that satisfy the criterion in part (a) are suitable candidates? O Aluminum O Magnesium O Steel O Tungsten O Copper O Brass O Titanium O Nickel