Draw the stress-strain diagram for any ductile and brittle material and explain thefollowing points:(a) Modulus of elasticity (b) Yield strength (c) Ultimate Strength (d) Ductility(e) Toughness

Stress -strain diagram of ductile and brittle material has to be explained.

Answered: ing points: odulus of elasticity (b)…

Engineering

Civil Engineering

ing points: odulus of elasticity (b) Yield strength (c) Ultimate

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.19P

See similar textbooks

Related questions

Q: QUESTION 3 The assembly consists of three steel rods and a horizontal bar BED. The structure…

A: Given P=36kN Area of EF = 625 mm^2 And AB,DC = 200mm^2 E = 200GPa Since the member BED is…

Q: 1. Determine the maximum tensile and compressive bending stresses in the beam shown. 4 kN/m 200 mm 1…

Q: P4: Two wooden boards are joined by cutting and gluing them together along the plane shown in the…

A: (a) If α=20° then, θ=90°-20°=70° The normal stress is calculated as,…

Q: Find the support reactions and joint force of the construction, shown on the figure, if: P=12 kN, q…

A: Finding out support reactions.

Q: 6. Value of Young's modulus of elasticity of steel if , Bulk modulus is 160 GPa and Poisson's ratio…

Q: The modulus of elasticity of mild steel is equal to •.... .. .... ... a. 2 x 10 N/m ' b. 2 x 10 N/m…

A: A modulus of elasticity is a quantity that measures the resistance of a material or element when…

Q: Two steel plates each of width 150 mm and thickness 10 mm are connected with three 20 mm diameter…

Q: The member shown in the right side consists of the steel rod AB that is screwed into the end of the…

Q: What is the value of reduction factor of the beam, if the stress in the steel is 400 MPa, and the…

Q: Cg Methed f Sectins loo kw determine forces in FE, FC bC ノ

A: Hello dear this is the solution of your problem The answer is found to be Force in members…

Q: 2. The manufactured wood beam carries the concentrated loads shown. What is the maximum safe value…

A: Solution Given Data working stress in shear= 6 MPa

Q: The strain in member AB was measured to be 8.9 x 104. If the member is an L3 X 2/2 x 1/4 of A36…

A: The following is the given information. Strain in member AB, ε=8.9×10-4 For A36 steel, Young's…

Q: A 26-foot-long structural steel bar is being tensed along its centroidal axis. Point B is being…

Q: An aluminum bar carries the axial loads at the positions shown. If E=70GPA, cumpute the total…

Q: If the steel has a stress of A100 = 100 ksi, what is the gross area of the steel required to design…

Q: AW 610 x 155 beam has two cover plates 400 x 20 mm thick placed on top and bottom of the section.…

A: Give properrties of W610 x 155 A = 19700 mm2 tw =12.7 mm…

Q: Which of the following is a deformation? Select one: a. Tension b. Shear c. Compression d. Strain

Q: section consisting of copper and steel carries compression force P. The properties of the materials…

Q: Compute the maximum force F (in KN) that can be applied to the composite rod if the allowable total…

Q: Two steel plates each of width 150mm and thickness 10mm are connected with three 20mm diameter…

Q: A composite bar is rigidly attached to the wall at A as shown in the figure. Axial loads are applied…

Q: The specimen shown has been cut from a -in.-thick sheet o vinyl (E = 0.45 x 10 psi) and is subjected…

Q: Compute the maximum force F (in KN) that can be applied to the composite rod if the allowable total…

A: The given figure is shown below:

Q: PROBLEM 1) An aluminum bar carries the axial loads at the positions shown. If E=70GPA, compute the…

Q: Solve for the design strength. Is it stable or not?

Q: Two T-shape sections are welded together to create a composite l-beam section as shown below.…

Q: When designing a structural member, which of the following statements is FALSE? A. The allowable…

A: Asked 1. False statement in designing a structural member. 2. Safety factor. 3. L = 1000mm, d =…

Q: 4.a Determine the force in each member of the truss. State whether the members are in tension or…

Q: Determine

Q: PROBLEM 1) An aluminum bar carries the axial loads at the positions shown. If E=70GPA, compute the…

Q: For the beam shown, calculate (a) the maximum bending stress; and (b) the bending stress at a point…

Q: What is another term for bend? (A) flex B) compress fracture twist E stretch

A: The another term of bend is flex.

Q: what is the largest load P

Question

Draw the stress-strain diagram for any ductile and brittle material and explain the
following points:
(a) Modulus of elasticity (b) Yield strength (c) Ultimate Strength (d) Ductility
(e) Toughness

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: Given data

VIEW

Step 2: stress-strain curves

VIEW

Step 3: definition of terms

VIEW

Solution

VIEW

Step by step

Solved in 4 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
The shown figure represents the stress-strain relations of metals A and B during tension tests until fracture.Determine the following for the two metals (show all calculations and units):a. Proportional limitb. Yield stress at an offset strain of 0.002 in./in.c. Ultimate strengthd. Modulus of resiliencee. Toughnessf. Which metal is more ductile? Why?
The stainless steel specimen is shown in Figure 3 with tensile engineering stress-strain behaviour. a)Compute the modulus of elasticity. and Compute the yield strength at a strain offset of 0.002.
An aluminum alloy cylinder with a diameter of 76 mm and a height of 150 mm. is subjected to a compressive load of 220 kN. Assume that the mate-rial is within the elastic region and a modulus of elasticity of 75 GPa. a. What will be the lateral strain if Poisson’s ratio is 0.33?b. What will be the diameter after load application?c. What will be the height after load application?
A steel solid is subjected to following set of principal stresses: 01 = 300 MPa and o2 = 250 MPa. Assuming u = 0.25 and elasticity modulus as 2 x 10 MPa, calculate the strain energy per unit volume in N-mm. (Round off to 2 decimals places).
If Poisson's ratio is 0.42, the Modulus of rigidity is 70.4225 GPa, and the bulk modulus is 416.66 GPa, then the elastic modulus of elasticity is (3 Points) 300 GPa 300 MPa 200 MPa None 200 GPa
describe the terms: limit of proportionality, elastic stage, yield strength, ultimate tensile strength and fracture stress
A high-yield-strength alloy steel bar with a rectangular cross section that has a width of 37.5 mm, a thickness of 6.25 mm, and a gauge length of 203 mm was tested in tension to rupture, according to ASTM E-8 method. The load and deformation data were as shown in Table Using a spreadsheet program, obtain the following:a. A plot of the stress–strain relationship. Label the axes and show units.b. A plot of the linear portion of the stress–strain relationship. Determine modulus of elasticity using the best-fit approach.c. Proportional limit.d. Yield stress.e. Ultimate strength.f. If the specimen is loaded to 155 kN only and then unloaded, what is the permanent deformation?g. In designing a typical structure made of this material, would you expect the stress applied in (f) safe? Why?
Q2c) Listed in the table below is the tensile stress-strain data for different grades of steels. Utilizing the data given answer the three queries given below. Material Yield Tensile Strain at Fracture Elastic StrengthStrengthFractureStrengthModulus (MPa) (MPa) (MPa) (GPa) A 410 1440 0.63 265 410 В 200 220 0.40 105 250 C 815 950 0.25 500 610 D 800 650 0.14 720 210 E Fractures before yielding 650 550 1) Which will experience the greatest percent reduction in area? Why? 2) Which is the strongest? Why? 3) Which is the stiffest? Why?
PROBLEM 1 A steel rod with a cross sectional area of 150 mm? is stretched between two fixed points. The tensile load at 20°C is 5000 N. a.) What will be the stress at -20°C? b.) At what temperature will the stress be zero? Assume a = 11 .7 µm/m°C, and E = 200 Gpa *Show geometry of deformation ©sidewar