(1) Describe what is meant by the term cooling curve when phase diagrams areconsidered.(ii) Give a thermodynamic interpretation of the terms break and halt.(iii) Sketch an example of a phase diagram for a binary mixture of compounds A and B,which are solids at room temperature. The melting point of A is higher than that of B.The eutectic point is at 80 mol % A. Compound AB melts incongruently.(vi) Sketch a cooling curve at the composition where compound AB is formed.

(i) A cooling curve of a a substance is a graph of the variation of the temperature with time as it…

Answered: (i) Describe what is meant by the term…

Engineering

Mechanical Engineering

(i) Describe what is meant by the term cooling curve when phase diagrams are considered.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
12. List three geometrical and/or spatial characteristics of dispersed phase that influence composite properties. B. Calculation Problems 13. Consider 2.5 kg of austenite containing 0.65 wt% C, cooled to below 727 C.
If 20000 g of steam is condensed in 2106 cm³ at a pressure of 6 MPa a. What is the temperature (C)? b. In what state (state) steam? c. Draw it in the form of a phase diagram that you know
how do you find the composition based on the tempratures from the phase diagram, like the temp are 160 and 130 right but you did both the temp above 150 in the phase diagram, also in the last line under given you wrote 35% sn and 55% sn, shouldn't it be 55% bi
For the Pb-Sn phase diagram showing incomplete solid solution, which of the Hume-Rothery rules are violated.
In a melting point phase diagram what do you mean by the eutectic point? How does this affect the obtained melting point range?
The point in the phase diagram where the fusion curve, the vapor pressure curve, and the sublimation curve join is called the Question 4 options: melting point. critical point. double point. boiling point. triple point. A sample of an ideal gas is slowly compressed to one-half its original volume with no change in temperature. What happens to the average speed of the molecules in the sample? Question 5 options: It doubles. It halves. cannot be determined without more information. It quadruples. It does not change. Phase changes occur Question 6 options: as the temperature decreases. all of the above. none of the above. as the temperature remains the same. as…
From the phase diagram of the Fe-0.25wt%C alloy below, determine the phase fraction and elemental composition of the resulting phase immediately after solidification across the eutectoid line (725 C). a.alpha_eutectoid = 96.6 wt% and cementite = 29.85 wt% b.alpha_eutectoid = 96.6 wt% and cementite = 3.4 wt% c.alpha_eutectoid = 1.05 wt% and cementite = 29.85 wt% d.alpha_eutectoid = 29.85 wt% and cementite = 1.05 wt%