he results of sieve analysis are shown below. Sieve No. Opening Size (mm) Mass Retained (g) 4 4.75 10 2 32 20 0.85 65 40 0.425 94 60 0.25 122 80 0.18 150 100 0.15 220 200 0.075 35 Pan 10 etermine the coefficient of uniformity.

he results of sieve analysis are shown below. Sieve No. Opening Size (mm) Mass Retained (g) 4 4.75 10 2 32 20 0.85 65 40 0.425 94 60 0.25 122 80 0.18 150 100 0.15 220 200 0.075 35 Pan 10 etermine the coefficient of uniformity.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: 1. Complete the given table Sieve number Diameter(mm) Mass retained Cumulative Mass Percent Passing…

Q: QUESTION 7 A cube of brass* has sides of 0.10m. Determine th isplace the top of the block 1.2x10 m…

Q: What can you conclude?

Q: The shear stress acting on the failure plane is O 100 -100 O 200 -200 Question 4 The normal stress…

A: Given:Required:Shear and normal stress on the failure plane

Q: Problem A sample of a dry coarse grained material of 500 grams was shaken through a nest of sieves…

A: Size of sieve for which 60% of sand passes, D60=2mmSize of sieve for which 300% of sand passes,…

Q: Give the value of Plastic modulus for ISHB 250 @ 54.7 kg/m weight.

A: Brief concept introduction- ISHB 250 is the short name for the Indian Standard Heavy Weight Section…

Q: P P [1.75 in. ートーート→ P 5.75 in.

Q: Given the data below about the Axial Strain (%) vs Deviator Stress: Axial Strain (%), X Deviator…

A: Axial strain vs deviator stress curve data set is given. Lagrange interpolation is used to get any…

Q: A stone is fully submerged in water. It weighs 450 N in air and 200 N in water. Calculate the volume…

Q: Load (N) Deflection (mm) 0 0 4.903034 0.000346 11.416539 0.000802 18.337648 0.001251…

A: The data you provided is from a load-deflection test on a mortar specimen. It shows how much the…

Q: Stress analysis Task Question / Calculate the critical design loads applied to the Stirling Engine…

A: Please find the answer in the below attachments

Q: P01: Calculate the modulus of elasticity Ec for each case shown in table: E,=33w¹ √√, psi E=0.043w¹5…

A: Density and compressive strength of concrete samples are given asDensityCompressive strength, f'c180…

Q: 5-Draw the relationship between percent passing and sieve size. and discuss. 6-what are the cause of…

A: “Since you have asked multiple question, we will solve the first question for you. If you want any…

Q: 1. Calculate the individual percent at pan Individual Cunulative Seive (nn) Weight Retained Percent…

A: Given table-

Q: 650 600 550 500 450 400 350 300 250 200 150 100 50 0.002 0.004 0.006 0.008 0.01 0.012 0.014 0.016…

A: Stress loading and stress and strain relationship is given in the question and it has been asked to…

Q: is the total permissible variation in its size. Select one: O a. tolerance O b. dimension O c.…

A: Tolerance is the total permissible variation in the size of a dimension. Tolerance is the difference…

Q: Q5: A/A tensile test was conducted for a sample and the relationship between stress and strain was…

A: As per the guidelines of Bartleby we are supposed to answer only first three sub-parts of a…

Q: 2. The masses of the blocks are ma = 30 kg and mg = 70 kg. Between all of the contacting surfaces,…

Q: 2.Complete the following table related to sieve analysis:

A: Given: Sieve size Cumulative Mass retained (g) Mass retained on sieve (g) %retained Cumulative %…

Q: Test Data and result Sample # Age (days) R (mm) Area (mm^2) Q(N) о (MPa) 1 7 100 400000 7 100 410000…

A: Compressive strength is defined as the ratio of the compressive force applied per unit surface area…

Q: results shown in the Table below, Calculate the percent passing through each sieve. Plot percent…

A: Calculate the percentage of soil retained over each sieve, % retained = Weight of soil…

Q: Chemical Species Concentration (mg/L as CaCO) Nat 10.25 K+ 1.15 NH3* 1.39 Mn4+ 0.02 Ca2+ 168.00 Mg2…

A: Given data Chemical species Concentration To find out Hardness

Q: Given the following data: B. Compact Unit Weight Determination Fine Aggregate a. Weight of measure,…

A: Total weight of sample = (Weight of measure + sample) - (weight of measure) Total weight of sample =…

Q: Design Average Strength Strength (MPa) Specimen Diameter Batch No. Strength Age (days) (Mpa) Load…

Q: are the results of a sieve analysis. Opening Size (mm) Mass Retained (g) 4.750 28 2.000 42 0.850 48…

A: For this first draw semi log graph between sieve size and % finer Effective size is diameter of…

Q: 1. Given the results of an Atterberg limit test. Complete the test report which will include filling…

Q: From the results of a sieve analysis given below compute for the coefficient of uniformity Sieve No.…

A: To find the Coefficient of uniformity

Q: the modulus of elasticity the percentage elongation the percentage reduction in area

A: Initial Area, A1 =π4d12=π4192=283.385 mm2 Fracture Area, A2=π4df2=π416.492=213.457 mm2 1) The…

Q: A. A materials engineer conduct a Moisture Content Test. Here is the result Oven dry Sample (2DD +…

Q: a ga in tension with the following results: Applied 1 Strain Force (N) (mm) (%) 0 5.000 Stress (MPa)…

A: We…

Q: Question: A contractor want to select a steel bars (diameter 16 mm) produced from two factories (A…

A: "Since you have posted a question with multiple sub-parts, we will solve the first two sub-parts for…

Q: Determine modulus of elasticity if bulk modulus 75 MPa and value of poisson ratio 0.32

A: Given data : The value of bulk modulus K=75 MPa The value of Poisson's ratio μ=0.32 To find :…

Q: Assume that the top of a round sprue has a diameter of 100 mm and has a height of 300 mm. At the…

A: top dia(D)=100mmbottom dia(d)=25mmheight(h)=300mm

Q: The given Mohr circle represents the stresses shown in the below prism, use Mohr circle and the…

Q: Duestion: A contractor want to select a steel bars (diameter 16 mm) produced from two Eactories (A…

A: lower class upper class mid class no of sample mid class strength * no of sample…

Q: What will be the diameter of an indentation in (mm) to yield a hardness of 250 HB when a 500-kg load…

A: Given data: Hardness number=250 HB p=500 kg. sphere diameter=5 mm

Q: Percent Diameter Sieve Size Passing in mm (%) 4 4.760 23 10 2.000 19 40 0.420 18 100 0.149 200 0.074…

A: As per the data given, it can be concluded that the required information needed in the question is…

Concept explainers

Foundation construction

Question

The results of sieve analysis are shown below.
Sieve No.
Opening Size (mm)
Mass Retained (g)
4
4.75
10
2
32
20
0.85
65
40
0.425
94
60
0.25
122
80
0.18
150
100
0.15
220
200
0.075
35
Pan
10
Determine the coefficient of uniformity.
O 2.045
O 1.791
O 1.624
O 1.934

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Using the Table Below, what is the approximate value of the match line if k=100, Ec=6x10^6, J=4, and the rest is the same with the example. Concrete elastic modulus, E. (106 Ib/in²) 10 20 1200 1100 4.5 4.0 30 1000 40 900 3.0 800 50 2.2 700 60 600- 70 500 80 - 800 400 200 100 50 Effective modulus of subgrade reaction, k (Ib/in3) 20 10 90 100 Example: k = 72 Ib/in3 E = 5 x 106 Ib/in? R = 95% (ZR = -1.645) S = 650 Ib/in? J= 3.2 S, = 0.29 APSI = 4.2 - 2.5 = 1.7 W18 = 5.1 x 106 (18-kip ESAL) Solution: D = 10.0 inches (nearest half-inch, from segment 2) C4 = 1.0 10 sninpow ajajɔuon GuIvai) 's 'əunadna Load transfer coefficient, J ~ Drainage coefficient, Cí Match line
Asapp.
Som.
15. A long proportional MS test specimen was subjected to tension. Determine (Modulus of - Modulus of Toughness - Elongation percentage) if you know that : Resilience a. b. Elongation = 0.12 mm at load 3 tons. & Elongation = 2.2 mm at load 5 tons. Load at proportional limit= 4.5 tons & Max. load = 7.5 tons Modulus of elasticity E = 2000 t\cm². Gage length after failure Li = 207 mm. C. d.
Determine the uniformity coefficient and coefficient of gradation from the following data:
MECHANICS OF DEFORMABLE BODIES WRITE THE COMPLETE SOLUTIONS. UPVOTE WILL BE GIVEN. ANSWER IN 2 DECIMAL PLACES.
ANSWER THE PROBLEM GIVE WHAT IS ASKED, SHOW YOUR SOLUTION, AND BOX THE FINAL ANSWERS. WRITE IT ON A CLEAN PAPER CLEARLY. I WILL GIVE THE FEEDBACK RATING AS POSSIBLE, YOU CAN ANSWER IT. THANK YOU
Calculate the fineness modulus.
If the specimen is originally square and has dimensions of a = 4 in., b = 3 in., and a thickness of t = 0.4 in., determine its new dimension a' after the load is applied. Express your answer to six significant figures and include appropriate units. a' = 4.00737 μA Submit Previous Answers Request Answer Part B X Incorrect; Try Again; 5 attempts remaining 0 in Determine its new dimension b' after the load is applied. Express your answer to six significant figures and include appropriate units. μᾶ b= 3.00333 ? in Submit Previous Answers Request Answer ? X Incorrect; Try Again; 5 attempts remaining
Please help with the attached problem
5
Procedure: 1. Compression tests on specimens shall be made as soon as practicable after removal from the moist storage. A 28-day test shall be performed within +-20 hours of the 28thday. Test specimens shall be kept moist by any convenient method during the period between removals from moist storage and testing. They shall be tested in moist condition. 2. All test specimens for a given test age shall be broken within the permissible time tolerance prescribed below. TEST AGE PERMISSIBLE TOLERANCE 24 HOURS +-0.5 HOURS OR 2.1% 3 DAYS 2 HOURS OR 2.8% 7 DAYS 6 HOURS OR 3.6% 28 DAYS 20 HOURS OR 3.0% 90 DAYS 2 DAYS OR 2.2 % 3. With a clean rag or rush clean the bearing faces of the bearing blocks, test the specimens and exclusion controller (elastomeric cps). 4. Rest the specimen on the lower extrusion controller, place the top extrusion controller on the specimen, and check the spacing between the sides of the specimen and the extrusion controllers to ensure no contact between the cylinder…