Q3(1p)Determine values for the constants n and k for the recrystallization of copper (Figure 10.11) at 119°C.Write how calculate thos e?1-y-exp(-kr")10080135"C 119°C,113"C 102"C43°C6088"C402010102101Time (mir)(Logarithmic scale!Feorinted wth permissicn trom Metalungica Iransactions Vol. 168, 1950, a publication of Ire Vietallurgical Socictyof AIME. Warrerdale, PA. Adapted from B. F. Decker and D Harker, Recrystallization ir Rolled Copper."Trans. AIME 189, 1950 p. 888Percent recrystallized

Answered: Image /qna-images/answer/282352f2-2f4e-4e19-ac53-ba6925b5a364.jpg

Answered: Determine values for the constants n…

Determine values for the constants n and k for the recrystallization of copper (Figure 10.11) at 119°C. Write how calculate thos e?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Figure 1 shows the schematic representation of how a metal atom moves under an applied force during…

A: ***As per our company policy we are supposed to do only 1 Question if you need the rest part…

Q: Explain the concept of formation and stability of metal-complexes and its application for the…

A: Concept of formation and stability of metal complexes: A species that is formed between an ion of…

Q: Why are dislocations not considered thermodynamic equilibrium defects like vacancies? Explain by…

A: The relative interplay between entropy and enthalpy affecting the Gibbs free energy of the…

Q: A binary alloy having 28 wt% Cu and balance Ag solidifies at 779°C. The solid consists of two phases…

A: The Cu-Ag phase diagram is given below,

Q: What factors determine the Debye temperature of a particular element? Provide comments, with…

A: The debye temperature is the temperature above which quantum effects become less dominant and…

Q: Sketch a phase diagram for two soluble components. Show the melting tem-perature of each element.…

A: The simplest type of phase diagram for any system can be of two components that are soluble in both…

Q: Figure Q4 (b) displays the time-temperature cooling paths for a 1080 steel on an isothermal…

A: In the given diagram, it can be seen that for paths (i) and (ii), the final position lies below the…

Q: Find the average grain size for the microstructure. Assuming that the length of each line is equal…

Q: Determine a for copper at reference temperature of 17ºC, 31ºC and 48ºC. Use Tcopper = 234.5ºC.

A: Given Reference temperature 17ºC 31ºC 48ºC Temperature = 234.5ºC To find Temperature coefficient

Q: (a) Calculate the change in molarentropy of adamantium that is heated from 700°Cto 800°C. (b) What…

Q: Show that for homogeneous nucleation during solid state transformation the critical radius r* is…

A: Nucleation is defined as the localised development of an unique thermodynamic phase in a gas,…

Q: For a Fe-2.5 %C alloy , what is the temperature at which the first liquid forms on heating and also…

A: Given: Fe-2.5 %C alloy

Q: When the metal is cooled in a molten state, a grain boundary is generated. Figure out the process of…

A: Grain boundaries: These are the area or surface defects which creates the interface between two…

Q: The ability to form martensite increases with increasing the critical cooling rate Examples of…

A: 1. If the cooling rate such that, it just touches the nose of TTT diagram is called critical cooling…

Q: A 95cu-5AG copper-silver alloy is cooled slowly from 1100°C to 20°C. What phases at what…

Q: how does the following recrystallization percentage of metallic alloys after annealing is…

A: Introduction When cold-worked metal is subjected to recrystallization annealing, new grains can form…

Q: b) Estimate the yield stress of copper containing an array of equally spaced second phase…

A: Yield strength alludes to the pressure at which the event of a foreordained measure of super durable…

Q: I want to know the formula for calculating the molar entropy change of aluminium giving the initial…

A: The Clausius statement for the second law of thermodynamics states that it is not possible to…

Q: xaplin with illustrations, slip via dislocation motion (edge abd screw dislocation) and twinning

A: To explain: Slip via dislocation motion (edge and screw dislocation) and twinning.

Q: Define annealing. (a) What effects does it have on the microstructure? (b) How does this affect…

A: Annealing: Annealing is a heat treatment process used to increase the ductility and reduce the…

Q: Why is the grain boundaries oxidization more sever and are the 1st to be oxidized than the grain…

Q: Describe the cooling of a peritectic alloy with the concentration CO and sketch the microstructure…

A: The given figure is-

Q: A hypo-eutectoid steel sample has a mass of 538kg and a nominal carbon content of 0.57%. Sketch the…

A: From the given data,

Q: The melting points of copper (Cu) and aluminum (Al) are 10830C and 660 oC respectively. They form…

Q: Under what high temperature circumstances is a very small grain size detrimental, and under what…

A: The fine grain structure of a component can both be advantageous and detrimental in different…

Q: With the aid of high resolution electron microscope, image of edge dislocation was observed in…

A: Dislocations are caused by the deformation of crystalline materials, such as metals, which can cause…

Q: C/ Bismuth (Bi) was melted at 2710C and tin (Sn) was melted at 2320C. Bismuth and ten are formed a…

A: The bismuth - tin phase diagram is given below -

Q: How would I... Determine the composition of aluminum and silicon (%Al/%Si) to melt the Al-Si…

A: what you are looking for is the eutectic point in a eutectic reaction a liquid phase transforms into…

Q: Describe a-dislocations, c-dislocations and c+a dislocations, which may be possible in HCP crystals.…

A: "Since you have asked multiple questions, we will solve the second question (since first question is…

Q: Do you have an answer to Q3? "Determine values for the constants n and k for the recrystallization…

A: Given: Avrami equation: →y=1-e-ktnWhere y is the fraction which is transformed into…

Q: Part A Determine the horizontal component of reaction at the pin A. Neglect the thickness of the…

A: For the given system To determine (a) the horizontal component of the reaction at pin A (b) the…

Q: Explain the following, using dislocation theory: metal strengthening by: (a) grain size (b) solid…

A: Dislocation theory plays a crucial role in understanding various mechanisms of metal strengthening.…

Q: Heat treatment Normalizing Recovery Why Normalizing Difference between normalizing and annealing…

A: This question is about the process of heat treatment to reform the material properties according to…

Q: Please provide a detailed solution. Explanation required for the formula used.

A: The ASTM grain size number (n) is related to the magnification factor (M) and the number of grains…

Q: Water has a latent heat of fusion of -334 MJm, surface free energy of 0.195 Jim, and meting point of…

Q: 0-10) Compare the equilibrium spacing of two partial disiocations between an Al alloy (G=28GP2 bn…

A: Given Data: The modulus of rigidity for aluminum allow is G=28 GPa=28×109 Pa. The breadth for…

Q: Question 4 942 Which statement is correct? O Annealing destroy the gra Annealing can idecrease

A: Annealing is a heat treatment process in which the metal is heated to a specific temperature where…

Q: At longer annealing times at appropriate temperatures, larger grains consume smaller ones. Summerize…

A: Annealing - Annealing is a heat treatment process generally use for steel structures. In annealing…

Q: Sketch following modes of dislocation motion and name conditions that help them occur: 1. Cross slip…

A: Cross slip Cross slip is the process by which a screw dislocation can move from one slip plane to…

Q: Explain the following microstructures: -Lamellar -Bimodal -Equiaxed

A: To explain: a) Lamellar b) Bimodal c) Equiaxed

Q: Given that the expression for the equilibrium concentration of point defects are similar for pure…

A: Given ; that the expression for the equilibrium concentration of point defects are similar for pure…

Question

Q3(1p)
Determine values for the constants n and k for the recrystallization of copper (Figure 10.11) at 119°C.
Write how calculate thos e?
1-y-exp(-kr")
100
80
135"C 119°C,
113"C 102"C
43°C
60
88"C
40
20
10
102
101
Time (mir)
(Logarithmic scale!
Feorinted wth permissicn trom Metalungica Iransactions Vol. 168, 1950, a publication of Ire Vietallurgical Socicty
of AIME. Warrerdale, PA. Adapted from B. F. Decker and D Harker, Recrystallization ir Rolled Copper."
Trans. AIME 189, 1950 p. 888
Percent recrystallized

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1 Solution Part 1

VIEW

Step 2 Solution Part 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

do not provide wrong solution
Q4
To increase the hardness of a steel gear, it was carburized at 850oC by introducing 1.3%C at its steel surface. What will be the final carbon content 1.4 mm beneath the surface if this treatment was lasted for 26 hours. The initial carbon content of steel is 0.1%C. (gas constant is 8.31 j/mol.K)
Refer to the Time Temperature Transformation (TTT) diagram given in Appendix A: (i) Determine the resulting microstructure for 0.8% carbon steel if the steel is rapidly cooled from the y region to 280°C within 5 seconds. (i) If the resulting microstructure in Question 6b (i) above is reheat to 300°C within 1 minute and hold for 1 hour at remain temperature, then and then rapidly quenched to room temperature, determine its final microstructure. (ii) If the resulting microstructure in Question 6b (i) above is reheat to 300°C within 1 minute and hold for 16 minutes at remain temperature, then and then rapidly quenched to room temperature, determine its final microstructure. (iv) Arrange the mircostructures 6 (b) (i,i and i) from the lowest to the highest hardnes value. (v) Sketch the thermal history from Question 6b (i) to (ii) on a TTT diagram.
3- It has been determined that the microstructure of a steel consists of 80% pearlite and 20% ferrite. What is the C concentration of this steel? Explain by calculating
Give me right answer with short explanation
Identify the microstructures of each of expected to be found in each of these alloys 1095 furnace cooled from 1650 farenheight 1095 air cooled from 1650 farenheight 1095 water quenched from 1650 farenheight
What are dislocation densities, compare for deformed sample and heat treated of sample?
an alloy with an avg grain diameter of 0.053 mm is l16 MPa. When the grain diameter is 0.008Amm, the yeild strength goesupto 231 MPa.lf the yeild strength is 207MPA, what would the grain diameter be?
In process, the metal is heated to almost recrystallization temperature and then cooled at faster rate. O Hardening process O Tempering process O Annealing process O Normalizing process
5
Answer part b