An axially-loaded welded angular connection is shown SD-002 . The angular section 150 x 100 x 10 mm having an area of 2400 mm a gusset plate having a thickness of 10 mm. All steel is A 36 (Fy = 248 MPa, Fu = 400 MPa) and E (70) electrodes (Fu = 484 MPa) is shielded metal-arc welding process. Compute the value of "a" if T = 500 kN. (Please do not round-off to whole number the require use the exact (2 decimal) value.)

An axially-loaded welded angular connection is shown SD-002 . The angular section 150 x 100 x 10 mm having an area of 2400 mm a gusset plate having a thickness of 10 mm. All steel is A 36 (Fy = 248 MPa, Fu = 400 MPa) and E (70) electrodes (Fu = 484 MPa) is shielded metal-arc welding process. Compute the value of "a" if T = 500 kN. (Please do not round-off to whole number the require use the exact (2 decimal) value.)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q1-A shielded metal arc welding operation is performed on steel at E = 30 volts and I = 225 amps. The heat transfer efficiency fi= 0.85 and melting efficiency f₂=0.75. The unit melting energy for steel Um = 10.2 J/mm3. Solve for: (a) the rate of heat generation at the weld and (b) the volume rate of metal welded
The arm in the figure is combined with a rod with a diameter of d=30 mm and a neck (corner) weld with a thickness of a= 5mm to the rod wall.sourced with. The force acting on the arm is F=2 kN. The lengths are L1=L2=100 mm. Joined parts are made of St37-2 (ak=235 N/mm2) material. Welding is I. Quality and has no impact effect. Check if the source in zone A is safe. (S=1.5 V1=0.8)
Note: All dimensions are in mm E - 210 000 MPa (N/mm') F-13 IN 1. A bracket is shown in the figure. Calculate the stresses on the welding. The bracket welded by E7018 clectrode. Based on stresses calculations, calculate the design factor of safety ELECTRODE TENSILE NUMBER YIELD STRENGTH STRENGTH _(MPa) (345) (393) (462) (531) (MPa) E60xx (427) (482) (551) (620) A = 0.707h(b + 2d). E70xx i = b/2 ESOxx b+ 2d E90xx 2d3 (600) (737) - 2d?y + (b+2d)3² 3 E100xx (689) (827) %3D E120xx
An angle iron made of AISI 1040 CD steel is welded to metal as shown and loaded with a dynamic load varying between +40kN and +60kN. E70XX (Sut = 482MPa, Sy = 393MPa) will be used as the welding electrode. Find the factor of safety of the weld zone. Note: that both static and dynamic loads are applied to the source.
4. Design a welded connection to resist the loading shown below (service load). A double angle tension member, 2 L5x5x5/16, is connected to a 3/8 inch thick gusset plate with fillet welding. Fy = 50 ksi for the angles and Fy = 36 ksi for the gusset plate. Compute the size and length of welding on the side of angles based on LRFD and indicate the information on the sketch. 1 = %" 2L5 x 5 x h6 D = 30 k L= 75 k
Q3 (a) What are the methods used to obtain a good weld when welding steel when the carbon content is high? b Find the appropriate length of the weld joint shown in the figure if the force is equal to (60000lb) and the operating stress value is (60ksi) and the size of the weld is (1/4in).
3.) The diagram below shows a 5.5m long double angle brace which is connected by 6mm welding connection. The length of weld shown in the picture is 300 mm on the top and 100 mm on the bottom. The 2-L127x 89x6.4 are 300W steel and long leg back-to-back. The braces are to be welded to a 12 mm 350W steel gusset plate. Determine the factored tensile capacity of the angles. Any intermediate connections that are required should also be specified. 740 kN -12 mm Gusset Plate
The weldment shown in the figure is subjected to a static force of 100 kN. The hot-rolled steel bar has a thickness h=6 mm and is of AISI 1015 HR steel. The vertical support is AISI 1015 HR steel. The electrode is given in the table below. Use the welding code method. (a) is the weld metal strength satisfactory? (b) Is the attachment strength satisfactory? h h=6 mm b=60 mm d=90mm electrode=E6010 |-b- h F
5. A steel cylindrical air receiver with 5 feet diameter and pressure load of 180 psi, design stress of 9500 psi maximum. The pressure vessel is to be provided with a 1.5 in diameter drain valve installed at the bottom of the vessel and a safety pressure relief valve is installed either at the topmost or at the side with a pop-out rating of 200 psi. Assume a 100% weld joint efficiency. The lap welding tensile strength is 65,000 psi. Determine the bursting pressure of this air receiver. psi
Assume that two 1.5-mm thick steel sheets are being spot welded at a current of 4000 A and current-flow time is 0.3 s. Using electrodes 5 mm in diameter, estimate the amount of heat generated and the amount of heat required to melt the weld nugget. Use an effective resistance of 350 un. Take u= 9,7 Joule/mm Which one of the following are correct? O a. If the electrodes were 7 mm diameter, the amount of heat generated would decrease b. The amount of heat generated by the equipment is between 1600 to 1700 Joules c. The equipment has enough power to weld the steel sheets. d. The equipment does not have enough power to weld the steel sheets e. The amount of heat required is between 700 and 750 Joules
The design below is used for a bridge construction. All parts of the assembly are made of ASTM A36 steel and are welded with an E60 electrode. Under these conditions, the minimum size weld, according to table 20-4, should be: 5/16 3/16 3/8 1/4 1/2 5/8
A mild steel ammonia receiver is a cylinder 2 m in diameter with a pressure load of 1250 kPa and a design stress of 65 MPa. The lap welding tensile strength is 450 MPa and the weld -joint efficiency is assumed to be 100%. Compute the bursting pressure of the receiver in kN/m².