An arc welding operation on nickel performs a groove weld. The cross-sectional area of the weld is 36.0 mm?. The welding velocity is 3.5 mm/sec. The heat transfer factor is 0.75, and the melting factor = 0.65. The melting temperature of nickel is 1447 °C. Determine the rate of heat generation by the welding source to accomplish this weld.

An arc welding operation on nickel performs a groove weld. The cross-sectional area of the weld is 36.0 mm?. The welding velocity is 3.5 mm/sec. The heat transfer factor is 0.75, and the melting factor = 0.65. The melting temperature of nickel is 1447 °C. Determine the rate of heat generation by the welding source to accomplish this weld.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A GTAW operation is performed on low carbon steel, whose unit melting energy is 10.3 J/mm3. The welding voltage is 22 volts and the current is 135 amps. The heat transfer factor is 0.7 and the melting factor is 0.65. If filler metal wire of 3.5 mm diameter is added to the operation, the final weld bead is composed of 60% volume of filler and 40% volume base metal. If the travel speed in the operation is 5 mm/sec, determine (a) cross-sectional area of the weld bead, and (b) the feed rate (mm/sec) at which the filler wire must be supplied.
A corner fillet weld with cross sectional area of 75 mm is made using oxyacetylene welding. Material of the welded plates is low carbon steel (Um = 10.3 J/mm'. Travel speed at which the bead is formed = 5 mm/s. Assume that only 40% of the energy generated by the torch is used for melting the metal; the rest is dissipated. If heat of combustion for acetylene is= 54.8 MJ/m³ , determine the volume flow rate of acetylene required to perform this OAW operation.
During a TIG welding process, the arc current and arc voltage were 50 A and 60 V, respectively, when in the welding speed was 150 mm/min. In another process, the TIG welding is carried out at a welding speed of 120 mm/min at the same arc voltage and heat input to the material so that weld quality remains the same. The welding current (in A) for this process is
I need the answer as soon as possible
A fillet weld on low carbon steel has a cross‑sectional area of 25.0 mm2 and is 900 mm long. Determine (a) the amount of heat required to perform the weld, and (b) the amount of heat that must be generated by the heat source, if the heat transfer factor = 0.90 and the melting factor = 0.60?
An electron-beam welding operation will join two pieces of steel plate together. The plates are 2.5 cm thick. The unit melting energy is 8050 J/cm3. The diameter of the work area focus of the beam is 0.15 cm, hence the width of the weld will be 0.15 cm. The accelerating voltage is 30 kV and the beam current is 35 milliamp. The heat transfer factor is 0.70 and the melting factor is 0.55. If the beam moves at a speed of 125 cm/min, will the beam penetrate the full thickness of the plates
A resistance spot-welding operation is performed on two pieces of 1.5 mm thick sheet steel using 12000 amps current for a duration of 0.20 second. The electrodes are 6 mm in diameter at the contacting surfaces. Resistance is assumed to be 0.0001 ohms and the resulting weld nugget is 6 mm in diameter and 2.5 mm thick. The unit melting energy for the metal is 12 Jmm³. What portion of heat generated was used to form the weld?
A gas metal arc welding test is performed to determine the value of melting factor f₂ for a certain metal and operation. The welding voltage = 25 volts, current = 125 amps, and heat transfer factor is assumed to be = 0.90, a typical value for GMAW. The rate at which the filler metal is added to the weld is 0.50 in³ per minute, and measurements indicate that the final weld bead consists of 57% filler metal and 43% base metal. The unit melting energy for the metal is known to be 75 Btu/in³. (a) Find the melting factor. (b) What is the travel speed if the cross-sectional area of the weld bead = 0.05 in²?
A continuous fillet wild is used to weld two pieces of 7.0-mm-thick austenitic stainless steel plate in an arc-welding operation. The plates are joined at a 90° angle using an inside fillet corner joint. The velocity of the welding head is 6 mm/sec. Assume the cross section of the weld bead approximates a right angle isosceles triangle (a right triangle with the two legs and their corresponding angles equal) with a leg length of 4.5 mm. The length of the weld = 230 mm. The melting factor of the setup = 0.65, the heat transfer factor = 0.90, and the Tm for austenitic stainless steel = 1670°K. Determine (a) The amount of heat (in joules) required to melt the volume of metal in (b) The heat that , (c) The rate of heat generation required at the welding source to accomplish the weld this weld (filler metal plus base metal) must be generated at the heat source
The welding parameters to be used to butt weld a metal alloy are being evaluated. In order to set up the welding machine, the melting factor for the metal (f2) has to be determined. The welding machine can deliver 4000 watts of power and the heat transfer factor for the welding process (f1) is 0.9. The final weld bead consists of 8 0% filler metal and 40% parent metal. The melting temperature of the filler metal and the parent metal is the same 2540 deg F. The cross-sectional area of the weld bead is 0.5 sq inches. The rate at which filler metal is added to the weld is 1 cu inch per min. Conversion factor 1 Btu = 1055 J and 0 deg F = 460 deg R Calculate the melting factor.
Q1-A shielded metal arc welding operation is performed on steel at E = 30 volts and I = 225 amps. The heat transfer efficiency fi= 0.85 and melting efficiency f₂=0.75. The unit melting energy for steel Um = 10.2 J/mm3. Solve for: (a) the rate of heat generation at the weld and (b) the volume rate of metal welded
A shielded metal arc-welding operation is performed on austenitic stainless steel at a voltage = 25 volts and a current = 200 A. The heat transfer factor = 0.92, and the melting factor = 0.60. The unit melting energy of medium-carbon steel is 137 Btu/in3. Determine the (a) power in the operation, (b) rate of heat generation at the weld and (c) volume rate of metal welded.