An Aluminum-Copper alloy initially containing (0.4 wt% Cu) is placed and held in an atmosphere that gives a constant surface Aluminum concentration of (1.0 wt% ). If after (43 h) the concentration of copper is (0.55 wt%) at a position (4.0 mm) below the surface. What is the diffusion coefficient of copper in aluminum for the treatment conditions. erf(z) 0.70 0.6778 0.75 0.7112 0.80 0.7421 0.85 0.7707 0.90 0.7970

An Aluminum-Copper alloy initially containing (0.4 wt% Cu) is placed and held in an atmosphere that gives a constant surface Aluminum concentration of (1.0 wt% ). If after (43 h) the concentration of copper is (0.55 wt%) at a position (4.0 mm) below the surface. What is the diffusion coefficient of copper in aluminum for the treatment conditions. erf(z) 0.70 0.6778 0.75 0.7112 0.80 0.7421 0.85 0.7707 0.90 0.7970

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A diffusion couple of two metals, A and B, was fashioned as shown: Diffusion of A atoms A-B alloy B Diffusion of B atoms After a 690 hour heat treatment at 1120°C the concentration of A is 1.8 wt% at the 3.2 mm position within Metal B. At what temperature (in Kelvin) must the diffusion couple need to be heated to produce this same concentration at a 2.3 mm position after 690 h? The preexponential and activation energy values for the diffusion of A in B are 1.9 x 104 m²/s and 239 kJ/mol, respectively.
2. Based on the illustration given, the increase in stress concentration factor would depend on what factors? P b
[Decarburization] An FCC iron-carbon alloy initially containing carbon with the concentration, C0, is exposed to anoxygen-rich and virtually carbon-free atmosphere. Under the given conditions, the carbon diffuses from the alloy andreacts at the surface with the oxygen in the atmosphere, meaning that the carbon concentration at the surface position is maintained essentially at 0 wt% C. The subproblems are independent.(1) Determine the diffusion coefficient at the temperature T given below. Use T = 1250 °C(2) When the value of D is given below, what position will the carbon concentration be Cx after a treatment for thetime, t? Use D = 1.93 × 10−10m2 /s; C0 = 0.35 wt%; Cx = 0.11 wt%; t = 12 hr
The diffusion coefficient of Ni in Cu at 1025 C is 10-9 cm2 s-1. How long does it take for the mean square root of the distance to be 1 cm?
Problem 3 An FCC iron-carbon alloy initially containing 0.35 wt% C is exposed to an oxygen-rich and virtually carbon- free atmosphere at 1400 K (1127 °C). Under these circumstances the carbon diffuses from the alloy and reacts at the surface with the oxygen in the atmosphere; that is, the carbon concentration at the surface position is maintained essentially at 0 wt% C. (This process of carbon depletion is termed decarburization.) At what position will the carbon concentration be 0.15 wt% after a 10-h treatment? The value of D at 1400 K is 6.9 x 10¹¹ m²/s.
An FCC iron–carbon alloy initially containing 0.25wt% C is carburized at an elevated temperature and in an atmosphere wherein thesurface carbon concentration is maintained at 1.0 wt%. If after 55.0 h the concentrationof carbon is 0.35 wt% at a position 5.0 mm below the surface, determine thetemperature at which the treatment was carried out.
If the initial composition of the carbon steel is c0=0.3 wt%, calculate the carbon concentration (in wt%) at a distance 0.2mm from the surface of the component after 1 hour of decarburization.
Define the two units used to express the concentration atmospheric polhutants: parts per million (ppm) and Cu = . Covert 0.l ppm to Cu.
The diffusion coefficients for species A in metal B are given at two temperatures: D (m²/s) 7.81 x 10-17 7.70x 10-16 i (b) Determine the value of Do. (a) Determine the value of the activation energy Qd (in J/mol). i T (°C) 1030 i 1260 J/mol m²/s (Use scientific notation.) (c) What is the magnitude of D at 1180°C? m²/s (Use scientific notation.)
At approximately what temperature (in Kelvin) would a specimen of an alloy have to be carburized for 2.0 h to produce the same diffusion result as at 760°C for 13 h? Assume that values for Do and Qd are 1.3 × 10-4 m²/s and 135 kJ/mol, respectively. T= i K
At approximately what temperature (in Kelvin) would a specimen of an alloy have to be carburized for 2.1 h to produce the same diffusion result as at 920°C for 14 h? Assume that values for Do and Q are 3.7 x 10 m/s and 156 kJ/mol, respectively. T- K
You wish to carburize 0.2 wt% C steel ball bearings. The balls have a diameter of 2.5 mm. You anneal them at 930 °C in an atmosphere which fixes the surface carbon concentration at 1 wt% C. (a) How long will it take to raise the average C concentration to 0.6 wt% ? (b) What is the concentration at the centre of each ball at this time?