a. Determine the diffusion coefficient for zinc diffusing into copper at 200°C. b. Create a plot showing diffusion coefficient vs. temperature for zinc diffusing into copper over the range of 0°C to 600°C. Include a minimum of six data points (you may use Excel for the repetitive calculations). What does the shape of the curve tell you about the dependence of diffusion rate on temperature? c. Determine the diffusion coefficient for nickel diffusing into copper at 200°C. Explain why the value differs from that found in Part a.

a. Determine the diffusion coefficient for zinc diffusing into copper at 200°C. b. Create a plot showing diffusion coefficient vs. temperature for zinc diffusing into copper over the range of 0°C to 600°C. Include a minimum of six data points (you may use Excel for the repetitive calculations). What does the shape of the curve tell you about the dependence of diffusion rate on temperature? c. Determine the diffusion coefficient for nickel diffusing into copper at 200°C. Explain why the value differs from that found in Part a.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

2. You want to produce 70%(v/lv) rubbing alcohol in the laboratory. You poured 20L of distillate having a 99% (v/v) concentration into a barrel. You open the valve such that the solution exits the barrel at 10mL/sec into another container which is empty. Simultaneously, you pour distilled water into the barrel at a flowrate of 30mL/sec. After achieving the desired concentration, what is the concentration in percent by volume of the alcohol in the second container?
Calculate the value of the diffusion coefficient D (in m^2/s) at 694°C for the diffusion of some species in a metal; assume that the values of D0 and Qd are 5.6 x 10^-5 m^2/s and 177 kJ/mol, respectively. R=8.314 J/(mol*K)
The surface of a solid sphere is covered by a monolayer of receptors for a ligand. When the ligands diffuse to the surface of the sphere, they are captured instantaneously by the receptors. The ligand diffusion coefficient is 2.3*10-9m2/s. Assume the bulk concentration far away from the sphere is constant of 1.5nM and the sphere radius is 1.8 μm. (a) Find the total ligand flux onto the surface of the sphere. The answer is in the form of A*10-18 mole/s. Please enter the value of A in the box.
Define and briefly elaborate terms listed below, support your elaboration with mathematical equations and illustrations where necessary: Concentration boundary layer, Viscous boundary layer and Thermal Boundary Layer. Diffusion equation, Laplace’s equation and Poisson’s Equation for rectangular coordinates. Analogy between heat and mass transfer. Prandtl, Schmidt, Lewis, Nusselt, and Sherwood number. Mole fraction of species and mass fraction of species. Critical radius of insulation related to heat transfer in pipes.
Thermal conductivity, temperature and heat flux in a solid are, respectively, analogous to mass diffusion coefficient, concentration and mass flux. Choose an option: Real or False
Consider diffusion of hydrogen through a poly(dimethyl siloxane) (PDMSO) sheet 20 mm thick. If the permeability coefficient at 350 K is 1.31 x 10-10 [(cm STP)(cm)/(cm2-s- Pa)], compute the diffusion flux [(cm STP)/(cm2-s)) at 500 K. The hydrogen pressures at the two faces are 10 kPa and 1 kPa, which are maintained constant. Hint: Pw is the temperature independent coefficient i.e. it's the same for all temperatures. Use PM = PMo (- Qp / RT), Qp = 13.7 kJ/mol and R = 8.31 J/mol-K
The mass diffusion rate dm/dt across a boundary between two different metals is a function of the following variables1...... .2., and 4...
Too, I hi X=0 k, q=0 T(x) = ? Q Search X=L Ac (3) What is the heat transfer on x? Does it depend To0,2 h₂ (1) Devive the governing equation from the ID, Steady-state heat diffusion equation, Apply two boundary conditions and solve for the two unknown constants in the governing equation. Finally, you will get the expression of T(x). rate qx ? Page 2
5-15 Compare the diffusion coefficients of car- bon in BCC and FCC iron at the allotropic transformation temperature of 912°C and explain the difference.
شكنذرس
What temperature is required to obtain 0.4%C at a distance of 0.3 mm beneath the surface of a 0.22% C steel in 2h, when 1.1% C is present at the surface? Assume that the iron is FCC. (Please see figure 5.12 below for diffusion coefficient data. Please use your notes for a table of erf() function values table of erf() fun Diffusion coefficient D (cm²/s) 10-3 !! ! ! ! ! 10- 10-5 10-9 10-10 10-11 10-12 10-13 10-14 Temperature (°C) 2000 1500 1200 1000 900 800 700 600 wwwwwwwwwwwwwww in graphite Mg in MgO Ca in CaO H in FCC iron Cin FCC iron Fe in FCC iron Fe in BCC iron H in BCC iron 104 T(K) C in BCC iron Fe in FeO 500 10-15 4 5 6 7 8 9 10 11 12 13 Figure 5-12 The diffusion coefficient D as a function of reciprocal temperature for some metals and ceramics. In this Arrhenius plot, D represents the rate of the diffusion process. A steep slope denotes a high activation energy.
For the diffusion coefficient K = 0, the above equation becomes: If known: The flow velocity is constant, U = 0.5 m/s Channel length 1000m Δx = 100m Δt = 1000 sec When t = 0, the concentration along the channel is zero [C(C,0) = 0] The boundary conditions along upstream & downstream are 2 & 0 respectively Calculate the above equation using the concentration C(x,t) & carry out until Time step k-5 with scheme: a. Explicit b. Implicit