A tensile test specimen has a gage length = 50 mm and its cross-sectional area = 100 mm². The specimen yields at 48,000 N, and the corresponding gage length = 50.23 mm. This is the 0.2 percent yield point. The maximum load of 87,000 N is reached at a gage length = 64.2 mm Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. %3D

A tensile test specimen has a gage length = 50 mm and its cross-sectional area = 100 mm². The specimen yields at 48,000 N, and the corresponding gage length = 50.23 mm. This is the 0.2 percent yield point. The maximum load of 87,000 N is reached at a gage length = 64.2 mm Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. %3D

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

As Fast As you can Please mak sure the answer is correct 100% Please match the following to the appropriate areas or sublocations illustrated on the steel stress-strain curve shown below: (ultimate tensile stress- yield stress - repture stress) (4) The maximum stress point on the stress strain curve. (2) The point where the proportional limit ends and the moment the elastic limit of the specimen is reached, the specimen will return to its original state after the loading is removed. Typically occurs before the steel specimen starts to plastically yield. (5) The point at which the steel specimens has underwent necking and breaks. This typically occurs after the maximum stress is reached during the experiment.
Engineering materials
39)A tensile test specimen has a gage length=3.0 inches and a diameter= .75 inches. Yielding occurs at a load of 38000lbs. The corresponding gage length=3.0103 inches (neglect the .0.2% yield point). The maximum load of 54000lbs is reached at a gage length =3.453 inches. If fracture occurs at a gage length of 3.873inches, determine the percent elongation at fracture (Round to the nearest whole %)
Ql- mm ,length 40 mm. The final diameter 18 mm and length 45 mm. Draw the force-extension diagram and determine the following : a) Ultimate tensile strength, c) Modulus of elasticity, d) Percent elongation and e) Percent reduction in area. The following data collected from tensile test of a metal bar diameter 20 b) The fracture strength, Force - kN 75 90 | 105 120 131 125 110 25 50 4.7 Extension-mm 0.02 0.04 0.06 0.20 - 0.60 1.60 3.00 4.0 Fracture
Pleas very fast A square cross-section v-notched specimen of height 75 mm has each side of 13 mm has been selected to perform Charpy impact test. A v-notch of thickness 1.97 mm is made at the middle of the specimen length. Determine the cross-sectional area at notch. Cross-sectional area at notch (in mm2)
10. A standard steel specimen of 0.504" diameter elongated 0.0125" in an 8" gage length during a test where it was subjected to a tensile force of 6249 lb. If the specimen's gage length was measured to be 8.0025" after the test was over, what was the permanent plastic deformation? What is the elastic deformation and what is the modulus of elasticity of that metal? r PL AE
A copper specimen of Young's Modulus 122 GPa is subjected to a tensile test in a laboratory and the following data are obtained. a) Initial length of the Specimen = 363 mm; b) Initial diameter of Specimen = 10 mm; c) Yield Stress = 128 N/mm2; d) Ultimate Stress = 212 N/mm2; e) Fracture Stress = 180 N/mm2; %3D g) % of Elongation = 44 %; h) % of Reduction in area = 38 %.
I want the solution clearly
A piece of steel rebar is tested in tension to determine its mechanical properties. The length of the sample is 87.3 mm and the cross-sectional area is 52.1 mm². When stretched by 37.2 mm, the force measured is 14,884 N. At this point, the graph is non-linear, but no clear neck is visible. If the Poisson's ratio of the material is 0.281, calculate the cross-sectional area (mm²) at this point.
Load (N) Elongation (mm) In a tensile test of stainless steel, the following data were obtained: 7,200 11,250 13,500 16,200 18,900 20,200 20,700 13,200 24.90 0.0 0.505 2.03 5.08 10.16 15.24 21.80 The dimensions of the cylindrical specimen were initial length L₁= 50.8 mm and initial area A₁ = 35.8 mm² and the area at fracture was Ar = 10.0 mm². Plot the stress-strain diagram and determine the following: a) Modulus of elasticity b) The yield strength at a strain offset of 0.002 c) Ultimate strength d) Fracture strength
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 152 kN. - Length of the specimen is 20 mm. - The yield strength is 86 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 10 kN, iv) Young's Modulus if the elongation is 2.2 mm at 10 kN and (v) Final diameter if the percentage of reduction in area is 28 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm) Answer for part 7
I want to solve the required squares and their units of measurement in regularity, please