A silicon carbide rotor fractures at a stress level of 100 MPa. This material has a fracture toughness of 4 MPa(m)1/2. Estimate the external flaw size responsible for this behavior with a geometric factor of f = 1.12. Report your size in mm from the options below. 0.4 mm 0.406 mm 10 mm 1 mm
Design Against Fluctuating Loads
Machine elements are subjected to varieties of loads, some components are subjected to static loads, while some machine components are subjected to fluctuating loads, whose load magnitude tends to fluctuate. The components of a machine, when rotating at a high speed, are subjected to a high degree of load, which fluctuates from a high value to a low value. For the machine elements under the action of static loads, static failure theories are applied to know the safe and hazardous working conditions and regions. However, most of the machine elements are subjected to variable or fluctuating stresses, due to the nature of load that fluctuates from high magnitude to low magnitude. Also, the nature of the loads is repetitive. For instance, shafts, bearings, cams and followers, and so on.
Design Against Fluctuating Load
Stress is defined as force per unit area. When there is localization of huge stresses in mechanical components, due to irregularities present in components and sudden changes in cross-section is known as stress concentration. For example, groves, keyways, screw threads, oil holes, splines etc. are irregularities.
A silicon carbide rotor fractures at a stress level of 100 MPa. This material has a fracture toughness of 4 MPa(m)1/2. Estimate the external flaw size responsible for this behavior with a geometric factor of f = 1.12. Report your size in mm from the options below.
Given data
Stress = 100 Mpa
Fracture toughness = 4 Mpa(m)^(1/2)
geometry factor = 1.12
Find the external flow size
Step by step
Solved in 2 steps with 1 images