A mild steel specimen with an original length of 300 mm long is acted on with a tensile stress of 500 MPa. If the deformation is entirely elastic, compute the resultant elongation? The modulus of elasticity of mild steel is 200 GPa.

A mild steel specimen with an original length of 300 mm long is acted on with a tensile stress of 500 MPa. If the deformation is entirely elastic, compute the resultant elongation? The modulus of elasticity of mild steel is 200 GPa.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
A steel specimen is tested in tension. The specimen is 2 in. wide by 2.3 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 30 kips and fractured at 40 kips. a) Determine the tensile stress at yield and fracture; b) If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 2 the yield stress.
Engineering strain of a mild steel sample is recorded as 0.100%. The true strain is 1. 2. 3. 4. 0.010% 0.055% 0.099% 0.101%
A steel bar has a length of 2.5 m and cross-section of 200-mm x 100-mm. The modulus of elasticity of this material is 210 GPa and Poison's Ratio is 0.3. The change in width after applying a tensile force of 150 kN is?
The stress-strain curve for mild steel is shown in figure given below. Choose the correct option referring to both figure and table. R Q. R. S. T. U. S U Point on the graph Description of the point P. 1. Upper yield point 2. Ultimate tensile strength 3. Proportionality limit 4. Elastic limit 5. Lower yield point 6. Failure
A piece of Aluminum originally 213 mm long is pulled in tension with a stress of 844 MPa. If the deformation is entirely elastic, what will be the resultant elongation in mm? The modulus of elasticity of aluminum is 69 GPa. Round your answer to 2 significant figures.
A cylindrical specimen of some metal alloy having an elastic modulus of 101 GPa and an original cross-sectional diameter of 3.6 mm will experience only elastic deformation when a tensile load of 2430 N is applied. Calculate the maximum length of the specimen before deformation if the maximum allowable elongation is 0.41 mm. i mm
A mild steel bar has a gauge length of 80 mm and the total elongation is 0.08 mm, find the strain produced in it.
A cylindrical specimen of undeformed brass that has a diameter of 300 mm is elastically deformed to a tensile strain of 0.001. If the Poisson's ratio for this brass is O.35, what is the change in specimen diameter? O Decrease by 3.00 x 104 m O Decrease by 1.05 x 104 m O Increase by 1.05 x 104 m O Increase by 0.028 mm
"Engineering Stress-Strain Curve" for a low carbon steel obtained as a result of the tensile test test. In terms of plastic forming by drawing important points on it (rolling, forging, machining ... etc.) Explain its importance.
A steel plate used for polymer forming is to be bent into a circular shape having an inside radius of 10 m. What maximum thickness can be used for the plate if the normal stress is not to exceed 267 MPa? Assume that the modulus of elasticity for the steel is 201 GPa.
A hollow steel cylinder 3.5m which has an inside diameter and outside diameter of 55mm and 35mm. If the steel carry a load (17) KN find the stress in the cylinder also find the deformation in the cylinder if the Modulus of Elasticity is 90 GPA.