A material has a Yield Strength of 424.8 MPa and a UTS of 567.5 MPa. If a medium hard condition for this material is required, what would be the target Stress at which the material has to be cold work to meet this requirement?

Q: on as possible

A: given:σ1=100mpaσ2=100mpaσ3=0mpa

Q: Why does the brittle material fails in helicoidal shape and ductile material shears on right section…

A: introduction; brittle material fail in tension. and ductile material fail in shear because ductile…

Q: Find the Brinell hardness number of the material

A: To Find  Brinell hardness number of the material

Q: Define different types of stresses, strains and material constants.

A:

Q: Sut A material has the following properties: 400 MPa and n = 0.25. Calculate its strength…

A: To findCalculate the strength coefficient, K.GivenUltimate strength, Strain hardening exponent,

Q: shear yield stress of the

A: Given; Uniaxial yield stress of a material is ,σy=280 MPa Find shear yield stress of the material,…

Q: An aluminum bar (6061-T4) is initially 225.00 mm long at a temperature of 20 C. It is placed between…

A: Given:Initial temperature of aluminum, Ti=20o CFinal temperature of  aluminum, Tf=205o CCoefficient…

Q: (a) What is the indentation diagonal length when a load of 0.61 kg produces a Vickers HV of 450? i…

A:

Q: 50.800mm is pulled in tension. Using the load-extension characteristics of Table 1 sand answer A…

A: Given-Data:- Stainless-Steel Diameter =12.8mm Guage length = 50,800mm To-Find:- 1) Plot…

Q: If the ultimate strength of a steel rotating-beam test specimen was around 1600 MPa. Estimate the…

A:

Q: (a) Derive the value of Brinell hardness using a hard spherical indenter, which was developed by…

A: Solution:   Note: Dear Student! As per our guidelines, we are only allowed to answer a single…

Q: A high-strength steel was subjected to a tensile test. It failed under a stress of 1600 MPa with a…

A: given : σf=1600 MPaε=2.7%=0.027E=200 GPaσy=1400 MPa

Q: Describe the profile manufacturing process below and the final steps for making columns for the…

A:

Q: A part made from hot-rolled AISI 1212 steel undergoes a certain amount of cold-work operation. If…

A:

Q: Explain the importance of Poisson's ratio for any mechanical component used in industry. Use a…

A: Since you have asked multiple questions, we will solve the first question for you. If you want any…

Q: (a) The final length of the wire. (b) The true stress and true strain at this load. (c) The…

A: Given :The initial length of wire, Li = 3 mm.The initial diameter, di = 30 μm.The final diameter, df…

Q: If you could produce AISI 1020 steel with a grain size of 50 nm, what would be the expected yield…

A: Permissible stress is stress which produces due to pressure or forces which does not exceed the…

Q: A fatigue test was conducted in which the mean stress was 58 MPa and the stress amplitude was 225…

A: Given conditions, Mean stress σmean=58 MPa. Stress amplitude σamplitude=225 MPa.

Q: For a point on a steel specimen, the principal stresses are calculated as 1 = 200 MPa and 2 = -40…

A:

Q: A 3.048 m annealed rod with a cross-sectional area of 555 mm2 was extruded from a 5083-0 aluminum…

A: Given: The initial length of rod, Li = 3.048 m The final length of the rod, Lf = 3.0518 m The…

Q: Consider a metal rod with a critical resolved shear stress of 40 MPa for a specific crystallographic…

A: Given:The critical resolved shear stress = The angle between the normal to the plane and the applied…

Q: The strain hardening exponent and the strength coefficient for aluminum is 0.2 and 180 MPa…

A:

Q: Calculate Vickers Hardness for a material if pyramid diamond (d)= 0.41mm and applied * ?load…

A: Given data:

Q: Q4) number of cycles on the fatigue strength. What is meant by the endurance limit ? Sketch the S-N…

A: NOTE:- As per our company guidelines we are supposed to answer only one question. Kindly repost…

Q: Find the Brinell hardness number of the material if the indenter diameter is 10mm and the produced…

A:

Q: Calculate the rolling force required to hot reduce an AISI 1018 steel plate, 80 cm wide, from an…

A:

Q: Which predicts the lower yield strength for most combinations of applied stress––the Tresca or the…

A: Solution: The envelope formed by the Tresca yield criteria is Hexagonal. The envelope formed by the…

Q: The stress-strain relation shown in the Figure below was obtained during the tensile test of an…

A:

Q: Q6/ A material has a true stress -strain curve given by o=Kɛ", derive and calculate the true and…

A: Given data: σ=Kεnk=689.47 kPan=0.5 Need to determine the true ad engineering ultimate tensile…

Q: A material has a Yield Strength of 424.8 MPa and a UTS of 567.5 MPa. If a medium hard condition for…

A: Solution: Given Data: σy=424.8 MPaσut=567.5 MPa   To Find: Working range of stress

Q: (a) What is the indentation diagonal length when a load of 0.61 kg produces a Vickers HV of 450? i…

A: (a) The Vickers hardness number is The load is (b) The load is The diagonal length is

Q: B/A cylindrical piece of carbon-steel with dimension of 100 mm length and 10 mm diameter exposed to…

A:

Q: A steel bar which is 457 mm long is repeatedly loaded with 4500 kg in successive tension and…

A: L=457 mmm=4500 KgSyt=300 MPaSut=400 MPafatigue limit=306 MPaE=210 GPa

Q: the stress compressive. What would be the final temperature when heating starts at 20degC? The E of…

A:

Axial Load

When a bar of the uniform cross-section is acted by a load, such that the load acts along the longitudinal axis of the bar, such kinds of loadings are known as axial loadings. In general terms, a load is an external force acting on a component. An axial load acts perpendicular to the geometric cross-section of the component. Based on the direction of the application of the load, an axial load can be tensile or compressive. The analysis of bodies under the action of axial loads is generally studied under the branch of mechanics, known as statics.