A hypothetical sample that has a plane-strain fracture toughness of 27.0 MPa m
1/2
It has been determined that fracture results
at a stress of 122 MPa when the maximum internal crack length is 8.8 mm. For this same component and alloy, compute the
stress level at which fracture will occur for a critical internal crack length of 6.5mm
Record answers for each step

Expert Solution

Step by step

Solved in 3 steps

SEE SOLUTION Check out a sample Q&A here

Blurred answer

Similar questions

463388 Ms Bowen is curious about what type of tape is the strongest and decides to develop an experiment to find out. She decides to test packing tape, painters tape, and duct tape. She takes two pieces of cardboard and tapes them together using each type of tape. Then she hangs weights on the bottom to see which one will hold the most weight. When the tape lets loose, she records the mass that was hanging from the bottom. Use this information to answer questions about this experiment on this and the next page. The independent variable is: The dependent variable is:
2. Casson model was discussed in class in the context of blood rheology. This phenomenological model is often used to describe the shear stress vs. shear rate relationship in colloidal suspensions where particle aggregation might cause the measured viscosity to increase at low shear rates. In an experiment, data for the shear stress rand the applied shear rate S were fitted to the Casson model written below (in a slightly different form compared to that given in the lecture notes): √t=√₁+√as. (1) The best least square fit parameters to the experimental data were found to be 40 mPa for the yield stress and 2.5 mPas for the parameter a, which is referred to as the plastic viscosity. a. Using Eq. (1), derive an expression for the fluid viscosity u as a function of S. b. Plot the viscosity of the fluid as a function of S for 0.1s¹
Explain why ductile materials do not fail in a brittle manner even thoughthey have small flaws and crack present. If so, explain the process of ductilefracture of the materials.