(a) Describe brazing and soldering processes. (b) Two parts made of steel were joined by adhesive bonding as shown in Figure 1. Describe with the aid of sketch how the joint design can be improved for a stronger bond. Justify your answer. Figure 1 [Rajah 1]

(a) Describe brazing and soldering processes. (b) Two parts made of steel were joined by adhesive bonding as shown in Figure 1. Describe with the aid of sketch how the joint design can be improved for a stronger bond. Justify your answer. Figure 1 [Rajah 1]

Welding: Principles and Applications (MindTap Course List)

8th Edition

ISBN:9781305494695

Author:Larry Jeffus

Publisher:Larry Jeffus

Chapter33: Brazing, Braze Welding, And Soldering

Section: Chapter Questions

Problem 17R: What brazing or soldering process uses a machine similar to a spot welder to produce the heat...

See similar textbooks

Related questions

Q: 2) The loss of strength in HAZ of weld joints of work hardened Al alloys can be reduced by

A: Given: To determine the correct option Welding is a process of joining two similar metals with the…

Q: What does liquid-solid phase bonding mean and in which cases is it preferred over welding? What does…

A: The liquid-solid phase bonding is a joining technique that has been used to join a variety of…

Q: 3) Improper cleaning of faying surfaces during fusion welding of carbon steels will primarily lead…

A: Given:Fusion welding:This is the process to join two or many materials by heating them upto the…

Q: A resistance spot-welding operation is performed on two pieces of 1.5 mm thick sheet steel using…

Q: In one type of welding, electric charge flows between the welding tool and the metal pieces that are…

A: The welding process given in the question suggests that it is arc-welding. In arc-welding, the…

Q: What is a cold solder joint? Identify its causes, its appearance, and the means of correction.

Q: Two 3.5 mm thick metal (Um = 9.5 J/mm') sheets are being joined using resistance spot welding. To…

A: Given Data Thickness of plate = 3.5 mm Um=9.5 J/mm3 R = 140 microohms Time = 0.3 sec D = 5.5 mm t =…

Q: Provide a reasonable explanation for the following observation: a welded component made of Al…

A: The welding of metals can lead to many defects in the material, majorly because of the heat to which…

Q: QUESTION 1 In an arc welding operation, a groove weld has a cross sectional area=0.055 in2 and is 24…

Q: 5 An inexperienced welder has welded a structural beam together and cooled it rapidly under water.…

A: On cooling a metal rapidly after heating is similar to quenching process, which forms fine crystal…

Q: what is the thickness of the weld nugget assuming it has a uniform thickness?

A: I = 11000 A R = 0.000130 ohm t = 0.25s H = I2Rt = 11,0002 (0.000130)(0.25) = 3,930 J

Q: What is welding? What are the different types of welding? What are the symbols of welding?…

Q: In order to prevent oxidation and retain molten metal in stud welding which of the following is…

Q: Welding stainless steel is a complicated process because (uniform / intergranular / erosion)…

A: Stainless steel: An iron-based alloy that contains variable amounts of chromium is known as…

Q: Identify the conditions under which a brazed joint is likely to be “stronger” than the brazing…

A: Since you have asked multiple questions, we will solve the first question for you. If you want any…

Q: Resistance spot welding is performed on two plates of 1.5 mm thickness with 6 mm diameter electrode,…

A: The thickness of the plates d = 1.5 mmdiameter of the electrode D = 6 mmCurrent I = 15000 ATime…

Q: (c) An arc welding is performed to join two metal pieces. After the welding process, the product is…

A: As given the two metals are welded using arc welding then a fatigue test is done on it. Fatigue…

Q: A composite bar is fabricated by brazing aluminum alloy [E = 10.000 ksi] bars (1) to a center brass…

Q: A composite bar is fabricated by brazing aluminum alloy [E= 10,000 ksi] bars (1) to a center brass…

Q: What does liquid-solid phase bonding mean and in which cases is it preferred instead of welding?…

Q: Question 1.1 Identify the weld defect shown in Figure 1 below. Provide reasons for your selection.…

Q: (b) Illustrate the schematic diagram of shielded metal-arc welding process.

Q: What type(s) of bonding would be expected for each of the following materials: solid xenon, calcium…

A: Bonding of Materials: There are basically three types of material bonding. These include ionic,…

Q: (c) Two carbon steel workpieces were joined together by welding. The type of joint is butt joint.…

A: It is a production method that generally combines materials, metals, or thermoplastics to melt and…

Concept explainers

Crystalline Imperfections

The crystalline imperfections are described as the geometrical defects in the crystal due to incorrect arrangement of atoms, impurity, vacancy, and many more. It is not possible to achieve a perfect or ideal crystal, practically.

Question

(a) Describe brazing and soldering processes.
(b) Two parts made of steel were joined by adhesive bonding as shown in Figure 1. Describe
with the aid of sketch how the joint design can be improved for a stronger bond. Justify your
answer.
Figure 1
[Rajah 1]

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

HANDWRITTEN ANSWER PLS. What does liquid-solid phase bonding mean and in which cases is it preferred instead of welding? What does capillarity mean in this process?
What does liquid-solid phase bonding mean and in which cases is it preferred over welding? What does capillarity mean in this process?
3) Improper cleaning of faying surfaces during fusion welding of carbon steels will primarily lead to Wider heat affected zone O Higher residual stresses Entrapment of gases and formation of inclusions O Higher fracture toughness of weld joint
Two 3.5 mm thick metal (Um = 9.5 J/mm?) sheets are being joined using resistance spot welding. To achieve required strength, it is desired to form a weld nugget that is 5.5 mm in diameter and 4.0 mm thick. The weld duration will be set at 0.3 sec. If the electrical resistance between the surfaces is 140 microohms, and only onethird of the electrical energy generated will be used to form the weld nugget determine the current.
Describe different types of primary bonding with neat sketches.
Answer by true (T) or false (F) for the folling sentences 1. Fusion welding means that the two surfaces to be joined and the filler metal are meling during welding and then solidifying in similar menner to local casting process. 2. In oxyacetylene welding process, the welding is done using oxidizing flame only. 3. Explusive welding process produces strong joints of dissimilar materials that are not weldable by are. 4. Hot working leads to eliminating the porosity in the metal and increasing the strength and hardness. 5. Work hardening is a characteristic induced in the processing part because of the heat treatment.
What is staircase effect? A welding operation on an aluminum alloy makes a groove weld.The cross-sectional area of the weld is 30.0 mm2. The welding velocity is 4.0 mm/sec. Theheat transfer factor is [0.92+{AAA/(20+YY)}] and the melting factor is [0.48+{AAA/(20+YY)}], where AAA are the last three digits and YY are the first two digits of yourstudent ID. The melting temperature of the aluminum alloy is 667°C. Determine the rate ofheat generation required at the welding source.
A resistance spot-welding operation is performed on two pieces of 1.5 mm thick sheet steel using 12000 amps current for a duration of 0.20 second. The electrodes are 6 mm in diameter at the contacting surfaces. Resistance is assumed to be 0.0001 ohms and the resulting weld nugget is 6 mm in diameter and 2.5 mm thick. The unit melting energy for the metal is 12 Jmm³. What portion of heat generated was used to form the weld?
(c) An arc welding is performed to join two metal pieces. After the welding process, the product is subjected to fatigue test. Discuss which part of the weld joint will have high potential to experience fatigue failure.
5 An inexperienced welder has welded a structural beam together and cooled it rapidly under water. This has caused the grain structure to become brittle. The beam will be used in the construction of a building. Which heat treatment method would be best to make the weld suitable for its purpose? (A) Heat the weld to 700 degrees Celsius and allow to cool slowly. (B) Heat to around 600-650 and hold for an hour then allow to cool slowly. (C) Heating to 300 degrees Celsius and let cool. (D) Reheat the weld to below the austenitic range and quench under water.
In brazing process the joint strength is generally_ a welded joint. * None of the mentioned Larger than Smaller than Equal to Cast iron and steel pipes are produced by; * Plaster mold casting Centrifugal casting Investment casting Die casting
* Asiacell In. answer.html Bartleby By ENG2028 Bartleby Vip Post & Solution 2,605 Members, 987 Online https://t.me/eng2028 More Question In order to prevent oxidation and retain molten metal in stud welding which of the following is used? * Shielding gas Metal rings O Flux Ceramic rings O This is a required question Answer Given data The given question is on the concept of stud welding Solution Stud welding is a welding technique similar to flash welding which two metals are joined through faster with the help of ceramic rings.