A composite material that has boron fibers coated in aluminum has a density of 2.65 g/cm^3. The fibers have a Young's modulus of 380 GPa, and aluminum has a Young's modulus of 70 GPa. The density of the fibers is 2.36 g/cm^3 and the density of the aluminum is 2.70 g/cm^3. What is the volume of the matrix?

A composite material that has boron fibers coated in aluminum has a density of 2.65 g/cm^3. The fibers have a Young's modulus of 380 GPa, and aluminum has a Young's modulus of 70 GPa. The density of the fibers is 2.36 g/cm^3 and the density of the aluminum is 2.70 g/cm^3. What is the volume of the matrix?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A silk fiber vwith a mass of 1.14 g, shows under the microscope, a cross-sectional area of 0.35 cm² . Assuming a silk density of 1.3 ст3 what is the length in mm of such fiber? Provide your answer with 2 decimal positions and no units, i.e.: 2.21 or 4.10 or 12.00. Answer:
For a glass/epoxy lamina with a 70% fiber volume fraction using the properties in the tables provided below (a) Find the ultimate tensile strength. (b) Find the minimum and critical fiber volume fractions related to (a). (c) Find the compressive strength when the matrix undergoes extension mode and when the matrix undergoes shear mode, which one controls the compressive failure? Property Axial modulus Transverse modulus Axial Poisson's ratio Transverse Poisson's ratio Shear modulus Axial tensile strength Axial compressive strength Transverse tensile strength Transverse compressive strength Shear strength Epoxy Glass Units 3.4 85 GPa 3.4 85 GPa 0.3 0.20 0.3 0.20 1.308 35.42 GPa 72 1550 MPa 102 1550 MPa 72 1550 MPa 102 1550 MPa 34 35 MPa
From the attached image. Annotate and explain the phases of the polymer stress-strain curve.
Q1/A Prove that the volume of an FCC unit cell, Vc is; Vc = 16R³√2 B) Explain in general terms, why many polymers and some ceramic glasses have an amorphous or semicrystalline structure.
I need help on this
i need the answer quickly
What is the tensile strength of a composite fibre when its diameter is 20 microns and its critical fibre length is 30 microns? The strength between the fibre and matrix is 150 MPa.
Answer whats in the image, please and thank you
a. Calculate the average density of aluminum bronze (95% Cu, 5% Al) Density of Cu and Al are 8.94 gm/cm and 2.7 gm/cm', respectively. b. Calculate the average density of nickel bronze (60% Cu, 20% Ni, 20% Zn) Density of Ni and Zn are 8.91 gm/cm³ and 7.14 gm/cm³, respectively.
If Eg = 2.2 GPa is the bulk modulus of elasticity for water, what pressure is required to reduce a volume by 0.6 percent?
In the cubic structure, there are mainly 3 elastic constants including C11, C11, and C44. Now, in my simulation, the value of C11 is becoming very high due to applying pressure. So far, in the simulations I've done, it's reached around 570 GPa. If more pressure is induced, it could increase further. My question is, is this increase normal?
This is a follow up to my question and the answer you submitted. The equation you used for J is wrong, not sure how you got J=π32×Do4-Di4, the equation should be J=π/2×ro4-ri4 which is J=pi/2(50^4-40^4) = 5.8e+6 mm^4