A 0.25% C hypoeutectoid plain-carbon steel is slowly cooled from 950°C to a temperature just slightly below 723°C. (a) Calculate the weight percent proeutectoid ferrite in the steel. (b) Calculate the weight percent eutectoid ferrite and weight percent eutectoid cementite in the steel.

Q: Consider 2.4 kg of a 99.7 wt% Fe-0.3 wt% C alloy that is cooled to a temperature just below the…

A:

Q: What is its average carbon content in weight? What is the weight of total ferrite?

A:

Q: An engineer is making determinations on the best alloy of steel to use in cables for a cable-stayed…

A:

Q: The time temperature transformation diagram for a hypoeutectoid steel is given below. Describe the…

A: In order to convert from tempered martensite  to (ferrite + pearlite): it is necessary to heat…

Q: Determine the quenching and normalizing process temperatures of 2 different steels containing 0.6% C…

A: TO DETERMINE THE QUENCHING AND NORMALIZING PROCESS :- QUENCHING :- For hypo-eutectoid steel…

Q: 30 1 min 1h 1 day 1 month 1 year 204°C (400°F) 149°C (300°F) 121°C (250°F) 70 121°C (250°F) 500 20…

A: Times required at various temperature to achieve required tensile strength Temperature°c…

Q: Write a short representation of a high alloy steel with 0.15% C, 10% Cr, 8% Ni, 2% Mo and a small…

A: The short representation will start with a set of digits representing 100 times the percentage of…

Q: 1. What temperature does a Fe-C metal with less than 4 weight percent C melt at? 2. What…

A: The Iron-Carbon diagram is a plot between the carbon weight percentage in Fe on X-axis and…

Q: To what temperature should hypoeutectoid plain carbon steel be heated for hardening purposes…

A:

Q: Why does the tensile strength of steel, which contains only austenite at room temperature, differ…

A: Ans 1:-The final microstructural change in hot deforming process  of steel is the transformation…

Q: 7- Calculate the tensile strength of steel: ou = 700 * c% + 340 N mm ( for hypo eutectoid steel)

A:

Q: A 1.05% C steel is slowly cooled from 900 °C to temperature just slightly above 723 °C. Calculate…

A: From the iron-carbide diagram understand that γ is used for austenite and Fe3C for cementite. Draw…

Q: A steel alloy has a microstructure consisting of ferrite and coarse pearlite as shown in the figure.…

A: Given: Let us consider the given image, Let's determine the type of alloy and the type of heat…

Q: Hardness of steel greatly improves (a) annealing (c) normalising (b) cyaniding (d) tempering

A: As per given question Best heat treatment process forHardness of steel greatly improves

Q: Write a short representation of 0.15% C, 10% Cr, 8% Ni, 2% Mo and a small amount of Flywheel high…

A: composition will be like0.15%C , 10%Cr , 8%Ni ,2%Mo

Q: b) When this furnace-cooled AISI 1040 steel reaches room temperature, identify 1) the phase(s)…

A: Solution: Given Data:

Q: Briefly describe how precipitation hardening happens in Al alloys (how the microstructure evolves as…

A: Hello. Since your question has multiple sub-parts, we will solve first three sub-parts for you. If…

Q: A hypo-eutectoid steel sample has a mass of 538kg and a nominal carbon content of 0.57%. Sketch the…

A: From the given data,

Q: Determine the structural constitution of a steel with 0.4% carbon at 727ºC during its cooling.…

A: The iron-carbon phase diagram is a graphical representation of the phase behavior of an iron-carbon…

Q: lease solve as fast as. Don

A: Given-Information:- Hypereutectoid steel = 2.5 kgHeated upto temperature = 725°CFerrite = 1000 g…

Q: What is the role of austenitic gram size in martensitic transformations? Is austenitic grain size is…

A: Austenitic gram size The austenite grain is around 1–2 μm after the intercritical receding stage,…

Q: Draw Fe-C binary phase diagram and discuss martensitic transformation for 0.1C% and 0.5C% plain…

A: The iron- carbon phase diagram is given below -

Q: a) A 10g ball bearing sphere is made of a steel containing 2.0 wt% C. Suppose the ball is…

A:

Q: This equilibrium phase of steel only occurs at temperatures above 723° C: martensite ferrite…

A: Austenite

Q: What is the marcosopic structure of metallic in low carbon and then high carbon steels .

A: Given data:-  low carbon steels :-Low carbon steels contain less than 0.3% carbon high carbon…

Q: Consider 1.0 kg of a 99.4 wt% Fe-0.6 wt% C alloy that is cooled to a temperature just below the…

A:

Q: A material is required as heating elements for an electrical resistance furnace for heat treating…

A: The phenomenon of joule heating is used to create heat in resistive heating components. Due to…

Q: Name the phases present and calculate the amounts of these phases just above the eutectoid…

A: Name the phases present

Q: Given an iron-carbon alloy that is heated at 770°C and has been held at this temperature long enough…

A: As per Bartelby guidelines for answering multiparts, i am answering only three subparts. Given:…

Q: Nickel is extensively used in alloy steels for engineering purposes, generally in quantities up to…

A: Given: To find the most appropriate option.

Q: Consider an AISI 1045 ferrite and pearlite microstructure. The sample is initially heated to 845 deg…

A: In the tempering of steels, the primary goal is to reduce the brittleness that is often associated…

Q: Write a short representation of an automaton steel with 0.20% C, 0.28% S, 1.1% Mn and 0.2% Pb in its…

A: The first set of digits in the short representation of the alloy will contain hundred times the…