6) Chromium can be electroplated from aqueous potassium dichromate, with the reduction shown below. If a current of 6.0A and a voltage of 4.5V are used: Cr207' (aq) + 14H* (ag)+ 12e¯→ 2Cr(s) + 7H20 a) How many hours would it take to completely convert 215mL of 1.25M K2Cr2O7 to elemental chromium? b) How many kilowatt-hours of electrical energy are required to plate 1.00 g of chromium?

6) Chromium can be electroplated from aqueous potassium dichromate, with the reduction shown below. If a current of 6.0A and a voltage of 4.5V are used: Cr207' (aq) + 14H* (ag)+ 12e¯→ 2Cr(s) + 7H20 a) How many hours would it take to completely convert 215mL of 1.25M K2Cr2O7 to elemental chromium? b) How many kilowatt-hours of electrical energy are required to plate 1.00 g of chromium?

Chemistry

10th Edition

ISBN:9781305957404

Author:Steven S. Zumdahl, Susan A. Zumdahl, Donald J. DeCoste

Publisher:Steven S. Zumdahl, Susan A. Zumdahl, Donald J. DeCoste

Chapter1: Chemical Foundations

Section: Chapter Questions

Problem 1RQ: Define and explain the differences between the following terms. a. law and theory b. theory and...

See similar textbooks

Similar questions

37. Arrange C3H8(g), ZnS(s), and H2O) in order of increasing standard molar entropy at 25°C. O ZnSts < C3H8(@< H2O) O ZnSt < H2O < C3H8@] O CaHBle) < H2O < ZnS) O H2O < C3H8(g) < NaClis)
Calculate the half-cell potential of cadmium in 0.1 M CdCl2.
When [Pb²+] = 1.10 M, the observed cell potential at 298 K for an electrochemical cell with the reaction shown below is 0.683 V. What is the Cr³+ concentration in this cell? 3Pb²+ (aq) + 2Cr(s) [Cr³+] = → 3Pb(s) + 2Cr³+ (aq) mol/L
Given the cell notation Pt /Cl2(g)/Cl¯(aq) // Zn+2(aq)/Zn. How long, in seconds, will it take for 1.000 g Zn (at. mass= 65.38) to deposit in the cathode if 2.000 A of current is used?
Consider the following cell. Cr | Cr³+ (1.00 M) || Ni²+(1.00 M) | Ni & = 0.68 V (a) How many milligrams of metallic nickel would be plated on the cathode if a current of 0.16 A is drawn for 1.3 hrs? 4.0 2.3e2 mg (b) What is the Cr³+ concentration when the Ni²+ concentration has dropped to 1.0 × 10-4 M? 4.0 33 X M What is the cell potential at this point? 4.0 0.666 X V
34. A galvanic cell is constructed in which the overall reac- tion is Cr,O (aq) + 14 H0 (aq) + 61 (aq) –→ 2 Cr" (aq) + 3 12(s) + 21 H,O(() (a) Calculate AE for this cellI. (b) At pH 0, with [Cr,O ] = 1.5 M and [I] = 0.40 M, the cell potential is found to equal 0.87 V. Calculate the concentration of Cr*(aq) in the cell.
Chromium can be electroplated from aqueous potassium dichromate, with the reduction shown below. If a current of 5 A and a voltage of 4.5V are used: Cr20, (aq) + 14H+ (aq)+ 12e¯ → 2Cr(s) + 7H20 How many hours would it take to completely convert 215 mL of 1.11 M K2Cr207 to elemental chromium?
To improve conductivity in the electroplating of automo-bile bumpers, a thin coating of copper separates the steel from aheavy coating of chromium. (a) What mass of Cu is deposited on an automobile trim piece ifplating continues for 1.25 h at a current of 5.0 A? (b) If the area of the trim piece is 50.0 cm² , what is the thickness of the Cu coating (d of Cu =8.95 g/cm³)?
Consider the cell diagram: Sn|Sn+2 (aq)||NO(g)|NO3-(aq)|Pt(s) Identify the reducing agent (A)NO (B)Sn+2 (C)Pt (D)Sn
A current of 8.86×104 A is passed through an electrolysis cell containing molten KCl for 12.7 days.(a) How many grams of potassium are produced? _________g(b) How many liters of chlorine are collected, if the gas is at a temperature of 273 K and a pressure of 1.00 atm? _________L
What mass of Molybdenum (Mo) could be deposited by electrolysis of an aqueous solution of Mo2(SO4)3 for 125 min using a constant current of 12.0 A?
What mass of rhodium (Rh) metal will be deposited from a solution of Rh3+ ions by running electrical current through the solution at 0.500 A for 120.0 minutes?