15. The stress-strain curve for an elastic-plastic material is shown. After loading and unloading, a test specimen of the material had a permanent set of 0.004. What was the maximum stress reached in the material during testing?

15. The stress-strain curve for an elastic-plastic material is shown. After loading and unloading, a test specimen of the material had a permanent set of 0.004. What was the maximum stress reached in the material during testing?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a tensile test for an aluminum alloy, the sample is 2 inches long and 0.5 inches in diameter. The proportional portion of the tension stress-strain diagram for an aluminum alloy is shown below. It the diameter change of the sample was also monitored during the above test, and it was found that the lateral strain of the sample is 1/3 of its axial longitudinal strain, what is the Poisson' ratio of the material under test: ___. Calculate your answer to 2 decimal place.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 18 kN, iv) Young's Modulus if the elongation is 1.3 mm at 18 kN and (v) Final diameter if the percentage of reduction in area is 25 %. Solution: Initial Cross-sectional Area (in mm2) The Diameter of the Specimen (in mm) Final Length of the Specimen (in mm) Stress at the elastic load (in N/mm2) Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
25.4 kN tensile load is applied on a 320 mm long cylindrical rod having a diameter of 10 mm. The rod experiences neither plastic deformation nor an elongation of more than 0.9 mm. What is the Young Modulus of the material in GPa?
In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final) of specimen after tensile test was 264.327. The load which caused fracture was (122.5 KN). After fracture, the final length was 47.516mm The % reduction in area is * O 15.819% 18.819 O 17.819 O 20.819
1. Ductile materials are tougher than brittle ones II. Tensile tests are not used when the material is brittle III. Brittle materials reach much higher ultimate stresses in tension than in compression Which statement(s) given above is/are true?
Why are the other three materials still used?
This question is from the subject "Theory Of Elasticity"
tensile test uses a circular test specimen that has a gage length of 50 mm and diameter = 20 mm. During the test the specimen yields under a load of 100,000 N. The corresponding gage length = 50.5 mm. This is the 0.2% yield point. The maximum load of 180,000 N is reached at a gage length = 65 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage length of 73 mm, determine the ductility. i need clear ans by hand and solve very very fast in 20 min and thank you | DYBALA
11
1- In a stress-strain curve it is possible to characterize a material by analyzing it. Show a graph that has the elastic deformation, plastic deformation and the yield point, explain each of them and define their differences.
In the Tensile experiment, the function of a load cell is to: Select one: a. Measure the applied force. b. Measure the applied strain. c. Measure the applied stress. d. Measure the specimen elongation.
1. Define ultimate compressive strength. What are are the specific conditions of a compression test specimen? 2. Describe the difference in performing the compression test between a ductile material and a brittle material.