bagolSupplementalProblems ton Jaum 22511?1510.16 A-in.-diameter structural nickel steel specimen was subjectedto a tension test. After rupture it was determined that the 2-in.standard-l-gage length had stretched to 2.42 in. The minimumdiameter at the fracture was measured to be 0.422 in. Computethe percent elongation and percent reduction in area.

Answered: Image /qna-images/answer/cc14b15a-01b9-423d-b7cf-25d5d5f49a6b.jpg

10.16 A-in.-diameter structural nickel steel specimen was subjected to a tension test. After rupture it was determined that the 2-in. standard-gage length had stretched to 2.42 in. The minimum diameter at the fracture was measured to be 0.422 in. Compute the percent elongation and percent reduction in area.

10.16 A-in.-diameter structural nickel steel specimen was subjected to a tension test. After rupture it was determined that the 2-in. standard-gage length had stretched to 2.42 in. The minimum diameter at the fracture was measured to be 0.422 in. Compute the percent elongation and percent reduction in area.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Describe the type of fractures expected when pure aluminium and steel with 1.15%C specimens are loaded in tension to failure. Comment on the differences expected.
2. The Goodman diagram relates oa and om for fatigue failure after a specific number of cycles Nf, where da is the cyclic stress amplitude, and om the mean stress. For a steel specimen it is found that oa oa (0). [1- (om/OTS)] where Ors is the metal's tensile stress (375MPa), and oa (0)~0.450TS is the 107 cycle fatigue limit at zero mean stress. Assuming the specimen is cycled repeatedly between 0 stress and a peak stress, what is the maximum peak stress if failure in < 107 cycles is to be avoided? Ans: 233 MPa
A cylindrical specimen of 1018 steel having a diameter of 6.35 mm and a gauge length of38.1 mm is pulled in tension. Use the load-elongation characteristics tabulated below. Determine the yield strength (σy) at a strain offset of 0.002.
A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
A steel specimen is tested in tension. The specimen is 2 in. wide by 2.3 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 30 kips and fractured at 40 kips. a) Determine the tensile stress at yield and fracture; b) If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 2 the yield stress.
A steel component is subjected to alternate cyclical loading. The steel follows Basquin's law for high cycle fatigue, o, x N = C, (where the stress amplitude is in MPa). Ignore the geometric detail and assume that Marin's modifying factors are all equal to 1. You are given the minimum stress ain = -213 MPa, the maximum stress omax = 213 MPa. The material data are Tensile strength oUTS = 539 MPa, Basquin's constant c, = 875 MPa, Basquin's exponent a = 0.085. a) Calculate the stress ratio R, the stress amplitude o, in MPa and the mean stress am in MPa. The answers are acceptable with a tolerance of 0.01 for R and of 1 MPa the stresses. R: MPa MPа b) Calculate the corresponding life, in 10° cycles, (tolerance of 0.1 106 cycles) N :
A steel specimen having a modulus of elasticity equal to 29x103ksi has a width of 1.0in and thickness of 0.25in. During the tensile strength testing, the specimen yielded at 12.5kips and fractured at 17.5 kips. Compute the value of the tensile stresses at yield and fracture
A Charpy V Notch test was conducted for a steel specimen. The average values of the test results at four different test temperatures were found to be 15 J at -45°C21 J at -18°C60 J at 5°C75 J at 40°CA bridge will be located in a region where specifications require a minimum of 35 J fracture toughness at 0°C for welded fracture-critical members. If the bridge contains a welded flange in a fracture-critical member, does the steel have adequate Charpy V notch fracture toughness to be used for this bridge?Show your supporting calculations.
A hot rolled steel tension test sample has a diameter of 6 mm and the original gage length of 30 mm. In a test to fracture, the stress and strain data below were obtained. Determine Generic Strain Value, %0.2 offset strain, and Calculated stress at %0.2 offset. Original diameter - 6mm Original Length - 30 mm Fracture diameter - 4.54 mm
The breaking strength of a 15.0 mm diameter bar was 540 MPa and the cross-sectional diameter after rupture was measured as 12.3 mm. Calculate the ductility in percent shrinkage and the actual stress at break.
A steel bar of 22 mm diameter and 8 cm gage length was axially loaded in tension and the following load deformation diagram was obtained. Determine: a) The yield strength by 0.2% off-set method. b) Modulus of elasticity by initial tangent method. c) Modulus of elasticity by tangent method at 2/3 of the yield strength. d) Modulus of elasticity by secant method at 70% of ultimate strength. e) Strain in fracture.