Question
Chapter 8, Problem 6ETSQ
To determine
The steel which is not quenched and tempered to increase the strength.
Expert Solution & Answer
Trending nowThis is a popular solution!
Students have asked these similar questions
i need quickly please please please
Which of these cast iron would allow the greatest amount of plastic deformation before fracture .
Nodular cast iron
Grey cast iron
White cast iron
None of them can be worked.
If the diameter of steel specimen stretched by tension load is doubled , then it’s tensile strength will be
Halved
Remain unaffected
Doubled
Become four times
Temperature is proportional with
Percent of elongation
Tensile strength
Modulus of elasticity
All above
The tensile strength of a steel specimen that have a 182 HB , equals to
490 MPa
910 MPa
627 MPa
Not given…
Which one of the following processes causes a dramatic increase in the hardness of a steel part?
A) quenching
B) tempering
(c) normalizing
D full annealing
A batch of casted mild steel has a modulus of elasticity of 200 GPa and a yield strength of 250 MPa. Calculate for its modulus of resilience. After cold working the steel, the yield strength increases to 310 MPa. Calculate for the percent reduction in the average grain diameter given σo = 70 MPa and k = 0.74.
Chapter 8 Solutions
Materials Science And Engineering Properties
Ch. 8 - Prob. 1CQCh. 8 - Prob. 2CQCh. 8 - Prob. 3CQCh. 8 - Prob. 4CQCh. 8 - Prob. 6CQCh. 8 - Prob. 7CQCh. 8 - Prob. 8CQCh. 8 - Prob. 9CQCh. 8 - Prob. 10CQCh. 8 - Prob. 11CQ
Ch. 8 - Prob. 12CQCh. 8 - Prob. 13CQCh. 8 - Prob. 14CQCh. 8 - Prob. 15CQCh. 8 - Prob. 16CQCh. 8 - Prob. 17CQCh. 8 - Prob. 18CQCh. 8 - Prob. 19CQCh. 8 - Prob. 20CQCh. 8 - Prob. 21CQCh. 8 - Prob. 22CQCh. 8 - Prob. 23CQCh. 8 - Prob. 24CQCh. 8 - Prob. 25CQCh. 8 - Prob. 26CQCh. 8 - Prob. 27CQCh. 8 - Prob. 28CQCh. 8 - Prob. 29CQCh. 8 - Prob. 30CQCh. 8 - Prob. 31CQCh. 8 - Prob. 32CQCh. 8 - Prob. 33CQCh. 8 - Prob. 34CQCh. 8 - Prob. 35CQCh. 8 - Prob. 36CQCh. 8 - Prob. 37CQCh. 8 - Prob. 38CQCh. 8 - Prob. 39CQCh. 8 - Prob. 40CQCh. 8 - Prob. 41CQCh. 8 - Prob. 42CQCh. 8 - Prob. 43CQCh. 8 - Prob. 44CQCh. 8 - Prob. 45CQCh. 8 - Prob. 46CQCh. 8 - Prob. 47CQCh. 8 - Prob. 48CQCh. 8 - Prob. 49CQCh. 8 - Prob. 50CQCh. 8 - Prob. 51CQCh. 8 - Prob. 52CQCh. 8 - Prob. 53CQCh. 8 - Prob. 54CQCh. 8 - Prob. 55CQCh. 8 - Prob. 56CQCh. 8 - Prob. 57CQCh. 8 - Prob. 58CQCh. 8 - Prob. 59CQCh. 8 - Prob. 60CQCh. 8 - Prob. 61CQCh. 8 - Prob. 62CQCh. 8 - Prob. 63CQCh. 8 - Prob. 64CQCh. 8 - Prob. 65CQCh. 8 - Prob. 66CQCh. 8 - Prob. 67CQCh. 8 - Prob. 68CQCh. 8 - Prob. 69CQCh. 8 - Prob. 70CQCh. 8 - Prob. 71CQCh. 8 - Prob. 72CQCh. 8 - Prob. 73CQCh. 8 - Prob. 74CQCh. 8 - Prob. 75CQCh. 8 - Prob. 76CQCh. 8 - Prob. 77CQCh. 8 - Prob. 78CQCh. 8 - Prob. 79CQCh. 8 - Prob. 80CQCh. 8 - Prob. 81CQCh. 8 - Prob. 82CQCh. 8 - Prob. 83CQCh. 8 - Prob. 84CQCh. 8 - Prob. 85CQCh. 8 - Prob. 86CQCh. 8 - Prob. 87CQCh. 8 - Prob. 88CQCh. 8 - Prob. 89CQCh. 8 - Prob. 90CQCh. 8 - Prob. 91CQCh. 8 - Prob. 92CQCh. 8 - Prob. 93CQCh. 8 - Prob. 94CQCh. 8 - Prob. 95CQCh. 8 - Prob. 96CQCh. 8 - Prob. 97CQCh. 8 - Prob. 98CQCh. 8 - Prob. 99CQCh. 8 - Prob. 100CQCh. 8 - Prob. 101CQCh. 8 - Prob. 102CQCh. 8 - Prob. 103CQCh. 8 - Prob. 104CQCh. 8 - Prob. 105CQCh. 8 - Prob. 1ETSQCh. 8 - Prob. 2ETSQCh. 8 - Prob. 3ETSQCh. 8 - Prob. 4ETSQCh. 8 - Prob. 5ETSQCh. 8 - Prob. 6ETSQCh. 8 - Prob. 7ETSQCh. 8 - Prob. 8ETSQCh. 8 - Prob. 9ETSQCh. 8 - Prob. 10ETSQCh. 8 - Prob. 11ETSQCh. 8 - Prob. 12ETSQCh. 8 - Prob. 13ETSQCh. 8 - Prob. 14ETSQCh. 8 - Prob. 15ETSQCh. 8 - Prob. 16ETSQCh. 8 - Prob. 17ETSQCh. 8 - Prob. 18ETSQCh. 8 - Prob. 19ETSQCh. 8 - Prob. 20ETSQCh. 8 - Prob. 21ETSQCh. 8 - Prob. 8.1PCh. 8 - Prob. 8.2PCh. 8 - Prob. 8.3PCh. 8 - Prob. 8.4PCh. 8 - The frame of a space shuttle type vehicle must...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- d) No increase Which of the following is not a property of steel materials? C a) Homogeneous and isotropic b) Linearly elastic stress-strain behavior c) Recyclable d) Fire-resistantarrow_forwardSteel, Brass, and Copper rods are connected as shown in the figure. Initially, the temperature was 15 degrees Celsius and the stress on the bars is zero. Eventually, the temperature increased to 25 degrees Celsius. Determine the total deformation on the brass. Steel Brass Copper Est = 200 GPa 12(10-)/°C apr Ebr Ecu 17(10-)/°C 120 GPa 100 GPa %3D ast = 21(10-6)/°C acu Acu = 515 mm? |Ast 200 mm2 Abr = 450 mm2 300 mm -200 mm 100 mm O -0.0109mm O 0.0241mm O -0.0241mm O 0.0109mm oooOarrow_forwardIn which cast-iron carbon exists in the form of Fe;C? A gray B white C) nodular (spheroidal) D malleablearrow_forward
- Which mechanism(s) cause(s) an increase in the strength of medium-carbon steels? A) decreasing the grain size B) strain hardening (c) heat treatment to provide martensitic microstructure D) Allarrow_forwardTask (3) you are asked to perform tensile test on specimens of two different materials (A and B) and you obtained the stress-strain diagram of the two specimens as shown in Figure 2: 400 350 300 250 Material A 200 150 100 50 0.02 0.04 0.06 0.08 0.1 0.12 0.14 0.16 0.18 Strain (mm/mm) 50 Material B 30 20 10 0.02 0.04 0.06 0.08 0.1 Strain (mm/mm) Figure 2: Tensile Test Analysis Stress (MPa) Stress (MPa)arrow_forwardTo get adequate strength and ductility for mild steel, up to What percentage of corbon content is required? а. 0.3 % b. 0.4 % О с. 1% O d. 0.6 %arrow_forward
- An AISI 1040 hot-rolled steel [E = 207 GPa; α = 11.3×10–6/°C] bar is held between two rigid supports. The bar is stress free at a temperature of 30°C. The bar is then heated uniformly. If the yield strength of the steel is 429 MPa, determine the temperature at which yield first occurs.arrow_forwardThe most common method for production of steel is Group of answer choices Slip casting Continuous casting Hot pressing Investment castingarrow_forwardThe yield strength for an alloy that has an average grain diameter of 4.4 x 10-2 mm is 133 MPa. At a grain diameter of 8.3 x 10-3 mm, the yield strength increases to 243 MPa. At what grain diameter, in mm, will the yield strength be 226 MPa? d = i mmarrow_forward
- a. Which of the following gives the approximate modulus elasticity of the The stress-strain diagram for a steel alloy having an original diam. of 12 mm and a material? gauge length of 50 mm is given in the figure. b. Which of the following gives the load on the specimen that causes yielding? c. Which of the following gives the ultimate load the specimen will (8) MPa ultimate strength- 80 support? 70 60 repture' strength yäerd põint- 50+ 40 propórtional limit 30 20+ 10+ 0 .0005 .001.0015 .002 .0025 .003 .0035 E(mm/mm)arrow_forwardMaterials, properties and testing Describe the effect bend testing have on the thermal properties of steel.arrow_forwardClearly show your workarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
The History of Iron and Steel; Author: Real Engineering;https://www.youtube.com/watch?v=7E__zqy6xcw;License: Standard Youtube License