Choose the correct answer for the following:thanhinhe to4. In rolling operation, large diameter roll induces.. on the surface of the rolled part.a. compression stress.5. the preheating treatment is not necessary if the carbon equivalent in the steel part is ..a. 0.3b. tension stress.c. no residual stressb. 0.6c. 0.8

Explanation : During rolling operation , due to rolling extrusion force applies over the surface to…

4. In rolling operation, large diameter roll induces.. on the surface of the rolled part. b. tension stress. 5. the preheating treatment is not necessary if the carbon equivalent in the steel part is ... b. 0.6 a. compression stress. c. no residual stress ...... a. 0.3 c. 0.8

4. In rolling operation, large diameter roll induces.. on the surface of the rolled part. b. tension stress. 5. the preheating treatment is not necessary if the carbon equivalent in the steel part is ... b. 0.6 a. compression stress. c. no residual stress ...... a. 0.3 c. 0.8

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: d) Plastic forming where uniaxial tensile and compression stress occurs in the material method is…

A: for d).In plastic deformation process in wire drawing and in deep drawing uniaxial tensile stress is…

Q: Rolling: A rolling operation is performed on a 5 mm thick sheet of low carbon steel (K=530, n=0.26…

A: Given:To find:

Q: You do a series of tensile tests on plates of a magnesium alloy that have been subjected to prior…

A: Given:To find:

Q: A 300 mm wide and 20 mm thick strip of Steel is fed through a rolling mill with two powered rolls of…

A: To find:a) Is rolling operation possible ?b) roll force requiredc) roll torque requiredd) input…

Q: Determine the value of the extrusion pressure (P/o) for the manufacture of a bar with a square…

Q: Pressure pads are used in rolling process. Select one: True False

Q: 1. In the bulk deformation process, there is a change in the thickness of the wokpiece. Thus, the…

A: 1)Explanation: Bulk deformation process like rolling , forming etc for constant thickness the length…

Q: Figure 1. shows the rolling operation. Determine the position bn. of the neutral point? Neglect…

Q: 3. During the rolling process, the average flow stress is 20,000 lb/in², determining the amount of…

Q: If it is desired to reduce the power required for the rolling operation of part (b), what…

A: Given : Roller operation for a workpiece To find : To reduce the power required

Q: 2. A rectangular prism with dimension of height, ho, length, 2Lo, width, Zo is forged to a final…

A: Disclaimer from Bartleby:Hello. Since you have submitted multiple questions, we will solve the first…

Q: 20. A forging process is shown at the figure below. Calculate the final diameter, if the initial…

Q: Fib the time period, if pure rolling is the condition

A: Given data: Roller connected to spring is released from the inclined plane To determine: Time…

Q: e) :- An extrusion Process is to Yeduce a 80mm long eylindrical billet from an initial diameter of…

Q: Which of the following method(s) reduce t roll separating force in a rolling process? i. Reducing…

Q: Please well explained with answers, not just formulas. Two cold roughing (thickness reduction)…

A: Given:To find:(a) Coefficient of friction.(b) Power required for 2nd rolling operation.(c) Yield…

Q: 19.3. A series of cold rolling operations are to be used to reduce the thickness of a plate from 50…

Q: For Forging and Rolling operations which of the following properties is important? a. Malleability…

A: Option a is correct malleability Malleability - Malleability is property of material which…

Q: Why are the internal stresses not produced in both working process ?

A: In this problem, it is asking why are the internal stresses not produced in hot working process.

Q: Question 7 7.1 A component is designed to be hot forged in an impression die. The projected area of…

Q: In the direct extrusion method, the heated metal billet is placed into th die chamber and the…

A: Ans: In the direct extrusion method, the heated billet metal is placed into the die chamber, and…

Q: Q4: In Flat Strip Open Forging (FSOF) Process. A strip ingot of length (90.5mm), width (4.75cm), and…

A: Given: L=90.5 mmW=4.75 cmt0= 1.75 cmt=15 mmσy=280+110ε0.34μ=0.065 To find: Maximum plate pressure

Q: Explanation of the Forging process with drawing.

A: Forging :-

Q: q1)Work-parts that have low area to- volume ratio are called. Select one: a. Bulk b. Billets c.…

A: Given:

Q: A round disk of 200-mm diameter is blanked from a strip of 3.0-mm, half-hard cold-rolled steel whose…

A: Given data: d=200 mmt=3 mmτ=300 MPaAc=0.075 Need to determine the punch, die diameters and blanking…

Q: A compression test is performed on a 2” diameter by 5” long bar of an unknown metal. At the end of…

A: Given:d1=2 inl1=5 inl2=3.5 inK=250 MPan=0.4a)Volume before compression=volume after compression…

Q: a). Briefly explain the drop forging process with a neat diagram. b). Explain the wire drawing…

Q: A solid piece of steel 60 mm in diameter and 80 mm height is reduced in height by 50 percent with…

Q: ng stres ng stress

Q: Which of the following statement(s) is/are correct with respect to the distribution of roll pressure…

A: We are to know about the pressure distribution along the arc in rolling process

Q: Why are the internal stresses not produced in both working process ?

A: Hot and Cold Working Process

Q: Friction between .................. and .... ........... in direct extrusion more force requires. m)…

A: Given :- L) Friction between .................. and .... ........... in direct extrusion more…

Q: A 200 mm wide and 42.0 mm thick plate made of low carbon steel is to be reduced in one pass in a…

A: Given: The width of the plate, b1 = 200 mm The thickness of plate initially, t1 = 42 mm The increase…

Q: Compare the force required to draw (25mm×6mm) capper strip to 45% reduction of area with that…

Q: What is the true sliding strain for a low carbon steel bar which is doubled

A: Given:Low carbon steel

Concept explainers

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.

Question

Choose the correct answer for the following:
than
hinh
e to
4. In rolling operation, large diameter roll induces.. on the surface of the rolled part.
a. compression stress.
5. the preheating treatment is not necessary if the carbon equivalent in the steel part is ..
a. 0.3
b. tension stress.
c. no residual stress
b. 0.6
c. 0.8

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step 3

VIEW

Step by step

Solved in 3 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

A solid cylinder of diameter 100 mm and height 50 mm is forged between two frictionless flat dies to a height of 25 mm. What is the percentage change in diameter?
One of the following process can't be used in Bulk deformation: А. Wire and bar drawing Extrusion С. Bending D. Rolling 2 Trimming is the cutting operation to remove flash from closed die forging: True False B.
answer the questions
13) Hot rolling of mild steel is carried out a. At recrystallization temperature b. Between recrystallization temperature c. Above recrystallization temperature d. Between 100⁰C to 150⁰C
Manufacturing methods
Question 3 A rolling operation on a 250 mm wide, 8 mm thick, 1112 cold rolled steel takes place using hardened steel rolls with a surface finish of 0.03 um. The rolls have a diameter of 350 mm and rotates at 115 rpm. The final thickness of the plate is 6 mm and the entry speed of the plate is 1.8 m/s. Calculate: 3.1 The minimum coefficient of friction required, that will make the rolling operation possible. 3.2 The required roll force. 3.3 The position of the neutral point, xn 3.4 Indicate, using a sketch, the neutral point showing all relevant notation and dimensions.
Manufacturing processes question.
Q1 Fill in the blanks 1. Punch manufactured from.....................r use in mass production 2. Hardness of the work piece is...............than the punch 3. Classification of types of sample Tensile Test..................and... 4. Metals ball is used in the Brinell test........... 5. An example of a corrosion resistant metal... and...
04: In Flat Strip Open Forging (FSOF) Process, A strip ingot of length (90.5mm), width (4.75cm), and initial thickness (1.75cm), is open forging to thickness (15mm). The mean flow stress o y 280+110, and friction facter (0.065), Determine the maximum plate pressure and the press capacity at. (1) forging anset. (II) forging end. 96.5mm
Bar stock of initial diameter = 90 mm is drawn with a draft = 15 mm. The draw die has an entrance
ANSWER FOUR QUESTIONS ONLY: QUESTION ONE: A cylindrical work piece is subjected to a cold upset forging operation. The starting piece is 80 mm in height and 50mm in diameter. It is reduced in the operation to a height of 40 mm. The work material has a flow curve defined by K-300 MPa and n=0.2. Assume a coefficient of friction of 0.1, assume that strain = 0.004, Determine the force as the process begins. at intermediate heights of 65mm, 55 mm, and at the final height of 40 mm.
Do please